[112]Cu-7Al单晶体循环形变行为Ⅱ.循环形变特征
, PP. 793-795
Keywords: 循环形变,硬化率,滑移方式,Cu－7Al单晶体
Abstract:
对「１１２」Ｃｕ－７Ａｌ单晶体的循环形变行为进行了研究.结果表明,其循环饱和应力－应变曲线与Ｃｕ单晶相似,在γｐ１＝１．１×１０＾－３－４．５×１０＾－３的范围内,存在和饱和平台,平台处的饱和应力为２７．３ＭＰａ；当γｐ２〈１．１×１０＾－３和γｐ１〉４．５×１０＾－３时,饱和应力均随应变幅的增大而单调升高.