TWIP钢中晶粒尺寸对TWIP效应的影响
, PP. 1083-1090
Keywords: TWIP钢,晶粒尺寸,加工硬化速率,加工硬化指数,TWIP效应
Abstract:
冷轧TWIP钢经1073,1173,1273和1373K固溶处理10min后,得到了晶粒尺寸分别为7,13,30和63μm的奥氏体组织.拉伸实验表明,随着晶粒尺寸的增加,加工硬化速率(dσ/dε)与真应变(ε)的变化关系由2阶段变为3阶段.当晶粒尺寸大于30μm时,加工硬化速率与真应变关系中的第2阶段对应的应变长度随着晶粒尺寸的增加而迅速增加.当真应变为0-0.2时,加工硬化指数随真应变的增加而迅速增加;在随后的变形中,与上述4个晶粒尺寸对应的试样的加工硬化指数分别稳定在0.47,0.53,0.56和0.68.OM和TEM观察显示,随晶粒尺寸的增大,变形过程中形变孪晶数量增多.对于较大晶粒尺寸的试样,形变孪晶在拉伸变形过程中形核的临界应力较低,随变形量增加,形变孪晶可持续形成,使其加工硬化能力增加,从而增大了TWIP效应;相反,晶粒尺寸减小使变形过程中的形变孪晶形核临界应力增大,抑制形变孪晶的产生,从而减小了TWIP效应.
| [1] | Frommeyer G, Br¨ux U, Neumann P. ISIJ Int, 2003; 43: 438
|
| [2] | Gr¨assel O, Kr¨uger L, Frommeyer G, Meyer L W. Int J Plast, 2000; 16: 1391
|
| [3] | Vercammen S, Blanpai B, Cooman B C D, Wollants P. Acta Mater, 2004; 52: 2005
|
| [4] | Bouaziz O, Guelton N. Mater Sci Eng, 2001; A319-321: 246
|
| [5] | Shiekhelsouk M N, Favier V, Inal K, Cherkaoui M. Int J Plast, 2009; 25: 105
|
| [6] | Christian J W, Mahajan S. Pro Mater Sci, 1995; 39: 1
|
| [7] | Ueji R, Tsuchida N, Terada D, Tsuji N, Tanaka Y, Takemura A, Kunishige K. Scr Mater, 2008; 59: 963
|
| [8] | Danaf E E, Kalidindi S R, Doherty R D. Int J Plast, 2001; 17: 1245
|
| [9] | Lu L, Shen Y, Chen X, Qian L, Lu K. Science, 2004; 304: 422
|
| [10] | Kalidindi S R. Int J Plast, 1998; 14: 1265
|
| [11] | Danaf E E, Kalidindi S R, Doherty R D. Metall Mater Trans, 1999; 30A: 1223
|
| [12] | Xiong R G, Fu R Y, Li Q, ZhangM, Li L. Iron Steel, 2007; 42: 61
|
| [13] | (熊荣刚, 符仁钰, 黎倩, 张 梅, 李 麟. 钢铁, 2007; 42: 61)
|
| [14] | Barbier D, Gey N, Allain S, Bozzolo N, Humbert M. Mater Sci Eng, 2009; A500: 196
|
| [15] | Sevillano J G. Scr Mater, 2008; 59: 135
|
| [16] | Meyers M A, V¨ohringer O, Lubarda V A. Acta Mater, 2001; 49: 4025
|
| [17] | Barnett M R. Scr Mater, 2008; 59: 696
|
| [18] | Allain S, Chateau J-P, Kahmoun K, Bouaziz O. Mater Sci Eng, 2004; A387-389: 272
|
| [19] | Allain S, Chateau J-P, Bouaziz O, Migot S, Guelton N. Mater Sci Eng, 2004; A387-389: 158
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|