热处理工艺对含Nb焊缝金属组织与力学性能的影响
, PP. 1063-1069
Keywords: Nb微合金钢,热处理工艺,焊缝金属,Nb添加,微观组织,力学性能
Abstract:
采用含Nb及不含Nb两种焊丝对高速列车转向架用S355J2G3钢板进行焊接,分析了焊态下接头各区域的性能差别,研究了合金元素Nb和焊后热处理制度对焊缝金属组织和性能的影响.结果表明焊缝金属的韧性是焊接接头性能的薄弱环节.焊态下Nb的加入提高了焊缝金属的强度,但对塑性和韧性无明显影响.经去应力退火后,不含Nb焊缝金属的强度降低,延伸率和冲击功升高,而含Nb焊缝金属的强度升高,延伸率和冲击功降低,退火后含Nb焊缝金属中NbC颗粒析出是影响焊缝金属组织和性能的主要因素.在焊后正火处理条件下,随着正火温度的升高,不含Nb焊缝金属的组织和性能均无明显变化,而含Nb焊缝金属的强度明显升高,延伸率和冲击功显著降低.严格控制正火温度是含Nb焊缝金属获得高强韧性的关键.含Nb焊缝中魏氏组织的含量随正火温度的升高而明显增多.电镜观察表明,经920℃正火处理后,焊缝中的NbC颗粒尺寸大于退火态焊缝金属中的NbC相,而在1200℃正火处理后NbC颗粒溶解消失.
| [1] | Beladi H, Hodgson P D. Scr Mater, 2007; 56: 1059
|
| [2] | Zhang Y Q, Zhang H Q, Liu W M, Hou H. Mater Sci Eng, 2009; A499: 182
|
| [3] | Thridandapani R R, Misra R D K, Mannering T, Panda D, Jansto S. Mater Sci Eng, 2006; A422: 285
|
| [4] | Pereloma E V, Timokhina I B, Russell K F, Miller M K. Scr Mater, 2006; 54: 471
|
| [5] | Zhang Z H, Liu Y N, Liang X K, She Y. Mater Sci Eng, 2008; A474: 254
|
| [6] | Park J S, Lee Y K. Scr Mater, 2007; 57: 109
|
| [7] | Shanmugam S, Misra R D K, Hartmann J, Jansto S G. Mater Sci Eng, 2006; A441: 215
|
| [8] | Yu Q B, Wang Z D, Liu X H, Wang G D. Mater Sci Eng, 2004; A379: 384
|
| [9] | Lee S J, Lee Y K. Scr Mater, 2005; 52: 973
|
| [10] | Chen G A, Yang W Y, Guo S Z, Sun Z Q. Acta Metall Sin, 2004; 40: 1079
|
| [11] | (陈国安, 杨王玥 , 郭守真, 孙祖庆. 金属学报, 2004; 40: 1079)
|
| [12] | Shanmugam S, Ramisetti N K, Misra R D K, Mannering T, Panda D, Jansto S. Mater Sci Eng, 2007; A460-461: 335
|
| [13] | Anumolu R, Ravi Kumar B, Misra R D K, Mannering T, Panda D, Jansto S G. Mater Sci Eng, 2008; A491: 55
|
| [14] | Nayak S S, Misra R D K, Hartmann J, Siciliano F, Gray J M. Mater Sci Eng, 2008; A494: 456
|
| [15] | Pereloma E V, Timokhina I B, Hodgson P D. Mater Sci Eng, 1999; A273-275: 448
|
| [16] | Yi H L, Du L X, Wang G D, Liu X H. J Mater Metall, 2005; 4: 295
|
| [17] | (衣海龙, 杜林秀, 王国栋, 刘相华. 材料与冶金学报, 2005; 4: 295)
|
| [18] | Lee K J, Lee J K, Kang K B, Kwon O. ISIJ Int, 1992; 32: 326
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|