晶体取向和载荷模式对Ni_3Al合金单晶体疲劳行为的影响
, PP. 1009-1014
Keywords: 晶体取向,复合型加载,Ni_3Al合金单晶体,疲劳开裂
Abstract:
在名义Ⅰ型和Ⅰ／Ⅱ复合型载荷下研究了晶体取向和加载模式对Ni3Al合金单晶体疲劳开裂行为的影响.结果表明疲劳开裂行为强烈地依赖于晶体取向和加载模式.在单晶体中，疲劳裂纹总是沿着具有最大切应力的滑移面开裂.根据单晶体的实验结果，解释了用三种主要的复合型断裂准则所预测的多晶体在复合型加载下的疲劳开裂行为.
| [1] | 1 Westbrook J H Trans Metall Soc AIME.1957:209:898
|
| [2] | 2 Flinn P A,Trans Metall Soc AIME 1960;218:145
|
| [3] | 3 Copley S M, Kear B H. Trans Metall Soc AIME,1967 239:977
|
| [4] | 4 Zhang G P,Wang Z G,Li G Y Acta Metall Mater,1997;45:1705
|
| [5] | 5 Kuruvilla A K,Stoloff N S.Scr metall ,1987;21:873
|
| [6] | 6 Matuszyk W,Camus G,Duquete D J,Stoloff N S ,Metall Trans,1990;21A:2967
|
| [7] | 7 Paris P C,Sih G C .ASTM STP 381,1965;30
|
| [8] | 8 Peach M D,Kochler J S Phys Rev,1950;80:436
|
| [9] | 9 Erdogan F,Sih G C .J Basic Eng.1963;85:519
|
| [10] | 10 Sih G C.Int J Fracture, 1974;10:305
|
| [11] | 11 Hussain M A、 Pu S L, Underwood J. ASTM STP 560,1974:2
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|