单晶镍基合金高温压缩蠕变的微观特征
, PP. 392-396
Keywords: 单晶镍基合金,压缩蠕变,位错分解
Abstract:
利用ＴＥＭ对「００１」取向单晶镍基合金高温压缩蠕变行为的研究表明γ’相沿应力轴方向形成筏状后,形变机制是〈１１０〉超位错切入筏状γ’相,（１／３）〈１１２〉超Ｓｈｏｃｋｌｅｙ不全位错自于「１０１」超位错的分解.领先和拖曳的超Ｓｈｏｃｋｌｅｙ不全位错形成的位错环阻碍了「１０１」超位错的继续扩展,是压缩蠕变应变量小的原因之一.