纯铝基复合材料的应力腐蚀与氢致开裂
, PP. 174-176
Keywords: 应力腐蚀,氢致开裂,纯铝,铝基复合材料
Abstract:
采用双悬臂梁（DCB）恒位移试验方法，Ⅱ型恒载荷试验方法以及慢为速率拉伸（SSRT）试验方法对纯Al复合材料的应力腐蚀与氢致开裂行为进行了研究，结果表明，在不发生应力腐蚀与氢致开裂的纯铝中加入20％（体积分数，下同）的SiC晶须或Al18O33晶须后就会发生应力腐蚀及氢致开裂.
| [1] | (姚红宇,花迎春,宋余九,涂铭旌.中国腐蚀与防护学报,1996;16:206)
|
| [2] | Chu W Y, Hsiao C M, Zhou X Z. Metall Trans, 1988; 19A;1067
|
| [3] | Chu W Y, Hsiao C M, Lie W X. Metall Trans, 1984; 15A:2087
|
| [4] | Chu W Y, Li J X, Huang C M, Wang Y B, Qiao L J.Corrosion, 1999; 55: 892
|
| [5] | Yu G H, Cheng Y H, Qiao L J, Wang Y B, Chu W Y.Corrosion, 1997; 53: 762
|
| [6] | Park J K, Lucas J P Scr Mater ,1997; 37: 511R
|
| [7] | Nair S V, Tien J K, Bates R C. Int Met Rev, 1985; 30:275
|
| [8] | Salasar De J M G, Urena A, Manzanedo S, Barrena M I.Corro Sci, 1999; 41; 529
|
| [9] | Chu W Y, Qiao L J, Chen Q Z, Gao K W. Fracture andEnviromental Fracture. Science Press. Beijing, 200O: 70
|
| [10] | (武扬,乔利杰,陈奇志,高克玮.断裂与环境断裂,北京科学出版社,2000:70)
|
| [11] | Yan S S, Mayer G. Mater Sci Eng, 1986; 82: 45
|
| [12] | McDanels D L. Corrosion, 1990; 46: 902
|
| [13] | Cao L, Li G F, Yao C K. J Chin Soc Corros Prot, 1990;10: 269
|
| [14] | (曹 利,李光福,姚忠凯,中国腐蚀与防护学报。199M;10:269)
|
| [15] | Shimizu Y, Nishimura T, Tamura M. Corros Eng, 1991;40: 406
|
| [16] | Yao H Y, Hua Y C, Song Y J, Tu M J. J Chin Soc CorrosProt, 1996; 16: 206
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|