阴极极化对LY12CZ铝合金腐蚀疲劳寿命的影响
, PP. 556-560
Keywords: 阴极极化,腐蚀疲劳寿命,铝合金LY12CZ
Abstract:
在LY12CZ铝合金腐蚀疲劳寿命曲线的基础上,研究了不同阴极电位下有无涂层试件在3.5%NaCl溶液中腐蚀疲劳寿命的变化规律.记录了一定阴极电位下阴极电流的变化情况.并通过对腐蚀疲劳断裂微观形貌的观察、分析,探讨了阴极极化对有无涂层保护的LY12CZ铝合金腐蚀疲劳寿命影响机理.
| [1] | Barter S, Sharp P K, Clark G. Eng Fail Anal, 1994; 1: 255
|
| [2] | KondoY. Corrosion, 1989; 45: 7
|
| [3] | Chen G S, War K C, Gao M, Wei R P, Flournoy T H. Mater Sci Eng, 1996; A219: 126
|
| [4] | Gangloff R P. In: Gangloff R P, Ives M B, eds., Proc First Int Conf on Environment-induced Cracking of Metals, Houston, Texas: NACE, 1990: 55
|
| [5] | Wei R P. Eng Fract Mech, 1970; 1: 633
|
| [6] | Gao M, Pao P S, Wei R P. Metall Trans A, 1985; 19A: 1739
|
| [7] | Ruiz J, Eliees M. Corros Sci, 1996; 38: 1815
|
| [8] | Wei R P, Pao P S, Hart R G, Weir T W, Simmons G W. Metall Trans, 1980; 11A: 151
|
| [9] | Weir T W, Simmons G W, Hart R G, Wei R P. Scr Metall, 1980; 14: 357
|
| [10] | Scamans G M, Alani R, Swann P R. Corros Sci, 1976; 16: 443
|
| [11] | Smith E F, Duquette D J. Metall Trans, 1986; 17A: 339
|
| [12] | Wanhill R J H, Deluccis J J, Russo M T. The Fatigue in Aircraft Corrosion Testing (FACT) Programme, AGARD Rep, 1989: 713
|
| [13] | Van de Ven E P G T, Koelmans H. J Electrochem Soc, 1976; 123: 143
|
| [14] | Grauer R, Wiedmer E. Werkst Korros, 1973; 24: 128
|
| [15] | Takahashi H, Kasahara K, Fujiwara K, Seo M. Corros Sci, 1994; 36: 677
|
| [16] | Kaesche H. Werkst Korros, 1963; 14: 557
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|