强磁场对Bi--6%Mn合金中MnBi相形态和相变的影响
, PP. 77-82
Keywords: 强磁场,Bi--Mn合金,铁磁相
Abstract:
在无磁场的条件下,降温过程中Bi--Mn合金在340℃发生包晶相变,顺磁性Mn1.08Bi相转变为铁磁性MnBi相,同时伴随着相的形态变化,由块状转变成片状;在10T磁场中,Mn1.08Bi相发生包晶相变的温度升高至介于360---370℃之间,且MnBi相晶体发生了分裂,分裂后的小晶体沿磁场方向定向排列和聚合。从磁场诱发应变的角度分析了磁场对相变温度和MnBi相形态的影响。
References
[1] | dde Rango P,Lee M,Lejay P,Sulpice A,Tournier B,Ingold M,Germi P,Pemet M.Nature,1991;349:770
|
[2] | BBraithwaite D,Beaugnon E.Nature,1991;354(14):134
|
[3] | FFarrel D E,B S.Phys Rev,1987;36B:4025
|
[4] | TTkaczyk J E,Lay K W.J Mater Res,1990;5:1368
|
[5] | CChen K,Maheswaran B,Liu Y P,Giessen B,Chang C,Markiewicz R.Appl Phys Left,1989;55:289
|
[6] | OOstertag C P,Shull R D,Vauolin M D,Blendell J E,Stearns L C,Fuller E R.Ceramic Supercond Ⅱ,1988:232
|
[7] | GGuo X,Altounian Z,Olsen J O S.J Mater Res,1990;5:2646
|
[8] | DDecarlo J L,Pirich R G.Metall Trans,1984;15A:2155
|
[9] | SShetty M N,Rawat D K,Rai K N.J Mater Sci,1987;22:19089
|
[10] | Yasuda H,Ohnaka I,Yamamoto Y.Mater Trans,2003,44:2207
|
[11] | Sugiyama T,Tahashi M,Sassa K,Shigeo A.Mater Trans JIM,1998;39:814
|
[12] | Wang H,Ren Z M,Deng K.Acta Matall Sin,2002,38:41(王晖,任忠鸣,邓康.金属学报,2002,38:41)
|
[13] | Guo X,Altounian Z,Str(?)m-Olsen J O.J Appl Phys,1991;69:6067
|
[14] | Li X,Ren Z M.Chin J Nonferr Met,2005;15:397(李喜,任忠鸣.中国有色金属学报,2005;15:397)
|
[15] | Moffatt W G.The Handbook of Binary Phase Diagrams.USA:Genium,1984
|
[16] | Liu Y.PhD thesis.Shanghai Institute of Ceramis,The Chinese Academy of Sciences,2004(刘岩.中国科学院上海硅酸盐研究所博士学位论文,2004)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|