锈层损伤对低碳贝氏体钢在含Cl-环境中腐蚀行为的影响
, PP. 442-449
Keywords: 低碳贝氏体钢,锈层,损伤,自修复
Abstract:
利用电化学、金相、能谱等方法,研究了低碳贝氏体钢在表面锈层受到不同程度的损伤后,在含Cl-环境中的继续腐蚀行为.实验发现,低碳贝氏体钢和作为对比材料的低碳钢试样的表面锈层受损伤后,在继续腐蚀过程中均能很快得到修复.在损伤程度与继续腐蚀时间相同的条件下,低碳贝氏体钢的锈层电阻与损伤修复率均高于低碳钢.低碳贝氏体钢基体/锈层界面的断裂韧性高于锈层本身.在受外界作用时,锈层不会沿基体/锈层界面彻底脱落从而在基体表面保存残留锈层.残留锈层能明显促进新锈层在损伤部位的形成.原有锈层与损伤部位新形成的锈层中Cu和Cr含量接近,并与钢基体的含量相当.
| [1] | Zhao Z Y. The Design of Alloy Steels. Beijing: National Defense Industry Press, 1999: 106
|
| [2] | (赵振业. 合金钢设计. 北京: 国防工业出版社, 1999: 106)
|
| [3] | Wang X M, Shang C J, Yang S W, He X L. Acta Metall Sin, 2002; 38: 661
|
| [4] | (王学敏, 尚成嘉, 杨善武, 贺信莱. 金属学报, 2002; 38: 661)
|
| [5] | Shang C J, Wang X M, Yang S W, He X L, Wu H B. Acta Metall Sin, 2002; 39: 1019
|
| [6] | (尚成嘉, 王学敏, 杨善武, 贺信莱, 武会宾. 金属学报, 2003; 39: 1019)
|
| [7] | Zhang Z G, Gu Z Y, Liao Y G, Guo Q L, Su F T, Chen Y Z. Electrochemistry, 2000; 6: 473
|
| [8] | (张志刚, 辜志俊, 廖永贵, 郭琦龙, 苏方腾, 陈衍珍. 电化学, 2000; 6: 473)
|
| [9] | Tan Y J, Bailey S, Kinsella B. Corros Sci, 1996; 38: 1545
|
| [10] | Nishimura T, Kodama T. Corros Sci, 2003; 45: 1073
|
| [11] | Nishimura T, Tahara A, Kodama T. Mater Trans, 2001;42: 478
|
| [12] | Lin C, Li X G, Liu X D. J Chin Soc Corros Prot, 2005; 25: 4
|
| [13] | (林翠, 李晓刚, 刘晓东. 中国腐蚀与防护学报, 2005; 25: 4)
|
| [14] | WanJ H, Wei F I, Chang Y S, Shih H C. Mater Chem Phys, 1997; 47: 1
|
| [15] | Han W, Wang J, Wang Z Y, Yu G C, Li H X. J Chin Soc Corros Prot, 2004; 24: 147
|
| [16] | (韩 薇, 汪俊, 王振尧, 于国才, 李洪锡. 中国腐蚀与防护学报, 2004; 24: 147)
|
| [17] | Nishimura T, Katayama H, Noda K, Kodama T. Corrosion, 2000; 56: 935
|
| [18] | Wang S T, Yang S W, Gao K W, Shen X A, He X L. Acta Metall Sin, 2008; 44: 1116
|
| [19] | (王树涛, 杨善武, 高克玮, 沈晓安, 贺信莱. 金属学报, 2008; 44: 1116)
|
| [20] | Liu L H, Qi H B, Lu Y P, Li X G. Corros Sci Technol Prot, 2003; 15: 86
|
| [21] | (刘丽宏, 齐慧滨, 卢燕平, 李晓刚. 腐蚀科学与防护技术, 2003; 15: 86)
|
| [22] | Choi Y S, Shim J J, Kim J G. J Alloys Compd, 2005; 391: 162
|
| [23] | Chi Y S, Shim J J, Kim J G. Mater Sci Eng, 2004; A385: 148
|
| [24] | Zhang Q C, Wang J J, Wu J S, Zheng W L, Chen J G, Li A B. Acta Metall Sin, 2001; 37: 193
|
| [25] | (张全成, 王建军, 吴建生, 郑文龙, 陈家光, 李爱柏. 金属学报, 2001; 37: 193)
|
| [26] | Matsushima I, Ueno T, Tamada A, Kubota H. Nippon Kokan Technol Rep, 1969; 46: 249
|
| [27] | Okada H, Hosoi Y, Yukawa K, Naito H. Tetsu-to-Hagan′e, 1969; 55: 355
|
| [28] | (岗田秀弥, 细井佑三, 汤川惠一,内藤浩光. 铁と钢, 1969; 55: 355)
|
| [29] | Misawa T, Yamashita M, Matsuda Y, Miyuki H, Nagano H. Tetsu-to-Hagan′e, 1993; 79: 69
|
| [30] | (三尺俊平, 山下正人,松田恭司, 幸英昭, 长野博夫. 铁と钢, 1993; 79: 69)
|
| [31] | Yamashita M, Miyuki H, Matsuda Y, Nagano H, Misawa T. Corros Sci, 1994; 36: 283
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|