固溶处理后冷轧变形7050铝合金时效工艺研究

DOI: DOI:10.3724/SP.J.1037.2009.00723, PP. 581-588

Keywords: 7050铝合金,冷轧,时效工艺,力学性能,显微组织

Full-Text   Cite this paper   Add to My Lib

Abstract:

7050铝合金固溶处理后经67%冷变形,在120℃一级时效时,冷轧引入的大量位错增加了样品强度,时效4h样品的强度比T6状态样品提高12.6%.随时效时间增加,位错导致的不均匀形核的析出相粗化,样品的拉伸强度逐渐降低.但时效32h样品的强度仍高于T6状态样品.冷轧后时效样品的晶界析出相与T6状态相比分布较为分散,并且随时效时间的增加逐渐粗化.120℃时效4h的样品,经165℃二级时效处理,随时效时间的增加,样品中残留位错大量湮灭,晶内、晶界析出相尺寸均逐渐增大,导致样品的强度逐渐降低,而延伸率逐渐升高,165℃时效6h样品的强度与T76样品相似.在135-180℃二级时效1h的样品中的位错密度随温度的升高而减小,同时晶内、晶界析出相尺寸随温度的升高而增大,导致样品强度逐渐下降.

References

[1]  Hatch J E. Aluminum Properties and Physical Metallurgy, Metals Park, Ohio: American Society for Metals, 1984: 1
[2]  Wagner J A, Shenoy R N. Metall Trans, 1991; 22A: 2809
[3]  Dai X Y, Xia C Q, Wu A R, Wang J W, Li Y Y. Mater Rev, 2006; 20: 104
[4]  (戴晓元, 夏长清, 吴安如, 王杰文, 李杨勇. 材料导报, 2006; 20: 104)
[5]  Starink M J, Wang S C. Acta Mater, 2003; 51: 5131
[6]  Dumont D, Deschamps A, Brechet Y. Mater Sci Eng, 2003; A356: 326
[7]  Kamp N, Sinclair I, Starink M J. Metall Mater Trans, 2002; 33A: 1125
[8]  Dixit M, Mishra R S, Sankaran K K. Mater Sci Eng, 2008; A478: 163
[9]  Sha G, Cerezo A. Acta Mater, 2004; 52: 4503
[10]  Wang D, Ni D R, Ma Z Y. Mater Sci Eng, 2008; A494: 360
[11]  Wang D, Ma Z Y. J Alloys Compd, 2009; 469: 445
[12]  Deschamps A, Brechet Y, Guyot P, Livet F. Z Metallkd, 1997; 88: 601
[13]  Kassim S, Rubaie A, Barroso E K L, Godefroid L B. Int J Fatigue, 2006; 28: 934
[14]  Waterloo G, Hansen V, Gjonnes J, Skjervold S R. Mater Sci Eng, 2001; A303: 226
[15]  Deschamps A, Livet F, Brechet Y. Acta Mater, 1999; 47: 281
[16]  Lin N A, Liu Z Y, Zeng S M. Trans Nonferrous Met Soc China, 2006; 16: 1341
[17]  Zhen L, Chen J Z, Yang S J, Shao W J, Dai S L. Mater Sci Eng, 2009; A504: 55
[18]  Wang D, Ma Z Y, Gao Z M. Mater Chem Phys, 2009; 117: 228
[19]  Hurley P J, Humphreys F J. Acta Mater, 2003; 51: 1087
[20]  Ou B L, Yang J G, Wei M Y. Metall Mater Trans, 2007; 38A: 1760
[21]  Nguyen D, Thompson A W, Bernstein I M. Acta Metall, 1987; 35: 2417

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133