初始取向对AZ31镁合金微观织构演化的影响
DOI: 10.3724/SP.J.1037.2010.00523, PP. 140-144
Keywords: 镁合金,初始取向,拉伸孪晶,微观织构演化
Abstract:
将从挤压棒材中截取的长轴与挤压方向分别成0o,45o和90o的AZ31镁合金长方体试样在中、高温度(523-723K)下沿长轴方向压缩变形,利用OM和SEM/EBSD技术观察和分析了初始取向对其微观织构演化的影响.结果表明,随着变形温度的降低,初始取向对变形行为的影响显著增加,在523K时,长轴平行挤压方向的0o试样在ε=0.06时拉伸孪晶体积分数可达30%,随着应变量的增加,孪晶体积分数持续增加,在ε=0.3时达到90\%;沿与棒材长轴夹角45o和90o截取的试样在ε=0.3时孪晶不足10%;拉伸孪晶的大量存在是0o试样出现急剧加工硬化的原因.0$^{\circ}$试样变形至ε=0.2时几乎所有的晶粒都发生了近90o的转动,基面由变形前平行于压缩方向转至与压缩方向垂直,45o试样只是在大应变时才发生晶粒的缓慢转动,而90o试样则几乎不发生晶粒转动.
| [1] | Liu Q. Acta Metall Sin, 2010; 46: 1458
|
| [2] | (刘庆. 金属学报, 2010; 46: 1458)
|
| [3] | Yang X Y, Jiang Y P. Acta Metall Sin, 2010; 46: 451
|
| [4] | (杨续跃, 姜育培. 金属学报, 2010; 46: 451)
|
| [5] | Koike J, Kobayashi T, Mukai T, Watanabe H, Suzuki M, Maruyama K, Higashi K. Acta Mater, 2003; 51: 2055
|
| [6] | Helis L, Okayasu K, Fukutomi H. Mater Sci Eng, 2006; A430: 98
|
| [7] | Yi S B, Davies C H J, Brokmeier H G, Bolmaro R E, Kainer K U, Homeyer J. Acta Mater, 2006; 54: 549
|
| [8] | Jiang J, Godfrey A, Liu W, Liu Q. Mater Sci Eng, 2008; A483-484: 576
|
| [9] | Yang X Y, Miura H, Sakai T. Mater Trans, 2003; 44: 197
|
| [10] | Jiang L, Jonas J J, Mishra R K, Luo A A, Sachdev A K, Godet S. Acta Mater, 2007; 55: 3899
|
| [11] | Al-Samman T, Gottstein G. Mater Sci Eng, 2008; A488: 406
|
| [12] | Yang P, Cui F E, Bian J H, Gottstein G. Trans Nonferrous Met Soc China, 2003; 13: 280
|
| [13] | Gottstein G, Al-Samman T. Mater Sci Forum, 2005; 495-497: 623
|
| [14] | Mark D N, Matthew R B. Scr Mater, 2004; 51: 881
|
| [15] | Yu K, Rui S T, Wang X Y, Wang R C, Li W X. Trans Nonferrous Met Soc China, 2009; 19: 511
|
| [16] | Nave M D, Barnett M R. Scr Mater, 2004; 51: 881
|
| [17] | Koike J, Sato Y, Ando D. Mater Trans, 2008; 49: 2792
|
| [18] | Al-Samman T, Gottstein G. Mater Sci Eng, 2008; A490: 411
|
| [19] | Li X, Yang P, Wang N, Meng L, Cui F. Mater Sci Eng, 2009; A517: 160
|
| [20] | Yang X Y, Zhang L, Jiang Y P, Zhu Y K. Chin J Nonferrous Met, in press
|
| [21] | (杨续跃, 张雷, 姜育培, 朱亚坤. 中国有色金属学报, 待发表)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|