Bi对AZ80镁合金凝固行为及显微组织的影响

DOI: 10.3724/SP.J.1037.2010.00604, PP. 410-416

Keywords: AZ80镁合金,Bi,凝固序列,共晶转变

Full-Text   Cite this paper   Add to My Lib

Abstract:

采用加热-激冷方法和OM,SEM,XRD,DSC等分析手段,研究了AZ80-Bi镁合金的凝固行为,分析了合金的凝固组织特征及其演变过程,阐明了合金的凝固序列.AZ80-2%Bi(质量分数)合金的铸态显微组织由α-Mg,β-Mg17Al12和Mg3Bi2相组成,其中Mg3Bi2相以片状和颗粒状两种形态存在.将2%Bi加入AZ80合金后,影响了合金的凝固序列,二元共晶转变L→α-Mg+β-Mg17Al12(437℃)被三元共晶转变L→α-Mg+β-Mg17Al12+Mg3Bi2(435℃)代替.2%Bi的加入使AZ80合金的初晶形核温度由568.8℃降低至562.6℃,共晶平台温度由424.2℃降到421.1℃.

References

[1]  Avedesian M M, Baker H. Magnesium and Magnesium Alloys. Materials Park, OH: ASM International, 1999: 22
[2]  Yang Z, Li J P, Zhang J X, Lorimer GW, Robson J. Acta Metall Sin (Engl Lett), 2008; 21: 313
[3]  Mordike B L, Ebert T. Mater Sci Eng, 2001; A302: 37
[4]  Tang W, Han E H, Xu Y B, Liu L. Trans Nonferrous Met Soc China, 2006; 16: 1725
[5]  Yakubtsov I A, Diak B J, Sager C A, Bhattacharya B, MacDonald W D, Niewczas M. Mater Sci Eng, 2008; 496: 247
[6]  Zhou J X, Wang B, Tong W H, Yang Y S. Acta Metall Sin, 2007; 43: 1171
[7]  (周吉学, 汪彬, 童文辉, 杨院生. 金属学报, 2007; 43: 1171)
[8]  Yang M B, Pan F S, Cheng R J, Tang A T. Mater Sci Eng, 2008; A491: 440
[9]  Hirai K, Somekawa H, Takigawa Y, Higashi K. Mater Sci Eng, 2005; A403: 276
[10]  Min X G, Zhu M, Sun Y S, Xue F. Mater Sci Technol, 2002; 10: 93
[11]  (闵学刚, 朱旻, 孙扬善, 薛烽. 材料科学与工艺, 2002; 10: 93)
[12]  Zhao Z D, Chen Q, Wang Y B, Shu D Y. Mater Sci Eng, 2009; A515: 152
[13]  Xie J C, Li Q A, Wang X Q, Li J H. Trans Nonferrous Met Soc China, 2008; 18: 303
[14]  Yuan G Y, Zhang W M, Sun Y S. J Southeast Univ, 1999; 29: 115
[15]  (袁广银, 张为民, 孙扬善. 东南大学学报, 1999; 29: 115)
[16]  Yuan G Y, Sun Y S, Zhang W M. Foundry, 1998; (5): 5
[17]  (袁广银, 孙扬善, 张为民. 铸造, 1998; (5): 5)
[18]  Yuan G Y, Sun Y S, Ding W J. Mater Sci Eng, 2001; A308: 38-44
[19]  Ren W L, Li Q A, Shi Y J, Zhang X Y. Rare Met Cem Carbides, 2010; 38(3): 34
[20]  (任文亮, 李全安, 石雅静, 张兴渊. 稀有金属与硬质合金, 2010; 38(3): 34)
[21]  Guo E J, Ma B X, Wang L P. J Mater Process Technol, 2008; 206: 161
[22]  Zhang G Y, Zhang H, Fang G L, Li Y C. Acta Phys Sin, 2005; 54: 5288
[23]  (张国英, 张辉, 方戈亮, 李昱材. 物理学报, 2005; 54: 5288)
[24]  Liu Z, Zhang K, Zeng X Q. Theoretical Basis and Application of Mg-based Lightweight Alloys. Beijing: Machine Industry Press, 2006: 61
[25]  (刘 正, 张奎, 曾小勤. 镁基轻质合金理论基础及其应用. 北京: 机械工业出版社, 2006: 61)
[26]  Massalski T B, Okamoto H, Subramanian P R, Kacprzak L. Binary Alloy Phase Diagrams. Materials Park, OH: ASM International, 1990: 759
[27]  Massalski T B, Okamoto H, Subramanian P R, Kacprzak L. Binary Alloy Phase Diagrams. Materials Park, OH: ASM International, 1990: 169
[28]  Willars P, Prince A, Okamoto H. Ternary Alloy Phase Diagrams. Materials Park, OH: ASM International, 1995: 2845
[29]  Wang C L. Phase Diagrams and Its Application. Beijing: Higher Education Press, 2008: 184
[30]  (王崇琳. 相图理论及其应用. 北京: 高等教育出版社, 2008: 184)
[31]  Han Q, Eenik E A, Agnew S R, Viswanathan S. in Hryn J, ed., Magnesium Technology, Warrendale, PA: TMS, 2001: 81
[32]  Gebelin J C, Suery M, Favier D. Mater Sci Eng, 1999; A272: 133

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133