外加电位对X80管线钢在鹰潭土壤模拟溶液中应力腐蚀行为的影响
DOI: 10.3724/SP.J.1037.2011.00046, PP. 1434-1439
Keywords: X80管线钢,应力腐蚀(SCC),外加阴极电位,土壤环境
Abstract:
采用电化学动电位极化技术、慢应变速率拉伸(SSRT)实验和SEM对X80管线钢在鹰潭土壤模拟溶液中的应力腐蚀行为进行了研究.结果表明X80管线钢在酸性土壤环境中具有较高的SCC敏感性,其断口模式为穿晶SCC;SCC机制随外加电位的不同而改变,在外加电位高于-930mV时,其SCC机制由阳极溶解和氢致腐蚀两种电极过程控制,呈现阳极溶解和氢脆复合机制;当电位低于该电位时,其SCC为氢脆机制.随着外加阴极电位的降低,X80管线钢的SCC敏感性不断增大;与X70钢相比,氢脆作用在X80管线钢SCC过程中发挥了更重要的作用.
| [1] | Liu Z Y, Li X G, Du C W, Zhai G L, Cheng Y F. Corros Sci, 2008; 50: 2251
|
| [2] | Zhai G L, Liu Z Y, Du C W, Li X G, Wang L X. Corros Prot, 2009; 30: 149
|
| [3] | (翟国丽, 刘智勇, 杜翠薇, 李晓刚, 王立贤. 腐蚀与防护, 2009; 30: 149)
|
| [4] | L¨u X Y, Wang Y, Li J C. Electr Weld Machine, 2009; 39(5): 121
|
| [5] | (吕向阳, 王义, 李景昌. 电焊机, 2009; 39(5): 121)
|
| [6] | Liang P, Du C W, Li X G, Chen X, Zhang L. Int J Miner, Metall Mater, 2009; 16: 407
|
| [7] | Gu B, Luo J L, Mao X. Corrosion, 1999; 55: 96
|
| [8] | Gu B, Yu W Z, Luo J L,Mao X. Corrosion, 1999; 55: 312
|
| [9] | Wang B Y, Huo L X, Wang D P, Deng C Y. J Tianjin Univ, 2007; 40: 757
|
| [10] | (王炳英, 霍立兴, 王东坡, 邓彩艳. 天津大学学报, 2007; 40: 757)
|
| [11] | Su D L, Feng Y, Chen J B. Mechanical Properties of Engineering Materials. Beijing: China Machine Press, 2005: 1
|
| [12] | (束德林, 凤 仪, 陈九磅. 工程材料力学性能. 北京: 机械工业出版社, 2005: 1)
|
| [13] | Chu W Y, Qiao L J, Chen Q Z. Fault Rupture and the Environment. Beijing: Science Press, 2000: 109
|
| [14] | (禇武扬, 乔利杰, 陈奇志. 断裂与环境断裂. 北京: 科学出版社, 2000: 109)
|
| [15] | Ogundele G I, White W E. Corrosion, 1986; 42: 71
|
| [16] | Zhang L F. J Iron Steel Res Int, 2006; 13(3): 01
|
| [17] | Garet M, Brass A M, Haut C, Solana F G. Corros Sci, 1998; 40: 1073
|
| [18] | Parkins R N. Corros Sci, 1980; 20: 147
|
| [19] | Liu Z Y, Li X G, Du C W, Zhai G C, Cheng Y F. Corros Sci, 2008; 50: 2251
|
| [20] | Cheng Y F, Niu L. Electrochem Commun, 2007; 9: 558
|
| [21] | Chen W, Fang K, Vokes E. Corrosion, 2002; 58: 267
|
| [22] | Liu Z Y, Zhai G L, Du C W, Li X G. Acta Metall Sin, 2008; 44: 209
|
| [23] | (刘智勇, 翟国丽, 杜翠薇, 李晓刚. 金属学报, 2008; 44: 209)
|
| [24] | Liu Z Y, Li X G, Du C W, Lu L, Zhang Y R, Cheng Y F. Corros Sci, 2009; 51: 895
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|