X80管线钢高pH应力腐蚀开裂机制与电位的关系
DOI: 10.3724/SP.J.1037.2012.00744, PP. 689-698
Keywords: X80管线钢,应力腐蚀开裂,高pH环境,外加电位,评价方法
Abstract:
采用慢应变速率拉伸实验和恒电位浸泡实验,分析了不同电位下X80管线钢在高pH环境中的应力腐蚀开裂(SCC)行为和机制.结合不同扫描速率下的动电位极化曲线的测量,从热力学角度对SCC的敏感电位区间进行了划分.在综合考虑材料的最大断裂强度和面缩率损失的前提下,提出了评价SCC敏感性的综合指标I∑,并将适用于酸性土壤模拟溶液中的SCC敏感性判据拓展到高pH环境中对其进行了验证.结果表明,X80钢在本实验溶液中的SCC敏感电位区间可以划分为-600—-569mV,受阳极溶解(AD)机制控制,沿晶应力腐蚀开裂(IGSCC)较为敏感,铁素体晶界优先溶解;在开路电位Eocp-—-600mV,SCC敏感性最低,以点蚀的发生和发展为特征,单纯的AD机制不会导致显著的穿晶应力腐蚀开裂(TGSCC)敏感性;在析氢电位-1046mV—Eocp,在AD和氢脆(HE)机制的共同作用下,X80钢的SCC敏感性最高,裂纹以TGSCC的形式扩展,点蚀对TGSCC裂纹的萌生和扩展起到关键作用;低于-1046mV,X80钢在HE的作用下断裂,表现出较高的脆性.经计算验证,采用I∑作为评价SCC敏感性的指标是可行的.
| [1] | (肖军, 吴明, 陈旭, 王成祥. 材料热处理技术, 2010; 39(18):28)
|
| [2] | Zhang L, Li X G, Du C W, Liang P. J Chin Soc Corros Prot, 2009; 29: 353
|
| [3] | (张亮, 李晓刚, 杜翠薇, 梁平. 中国腐蚀与防护学报, 2009; 29:353)
|
| [4] | Chen X, Wu M, He C, Xiao J. Acta Metall Sin,2010; 46: 951
|
| [5] | (陈旭, 吴明, 何川, 肖军. 金属学报, 2010; 46: 951)
|
| [6] | Parkins R N. Corros Sci, 1980; 20: 147
|
| [7] | Charles E A, Parkins R N. Corrosion, 1995; 51: 518
|
| [8] | Parkins R N. Corrosion, 1996; 52: 363
|
| [9] | Liu Z Y, Zhai G L, Du C W, Li X G. Acta Metall Sin, 2008; 44: 209
|
| [10] | (刘智勇, 翟国丽, 杜翠薇, 李晓刚. 金属学报, 2008; 44: 209)
|
| [11] | Liu Z Y, Wang C P, Du C W, Li X G. Acta Metall Sin, 2011; 47: 1434
|
| [12] | (刘智勇, 王长朋, 杜翠薇, 李晓刚. 金属学报, 2011; 47: 1434)
|
| [13] | Parkins R N, Zhou S. Corros Sci, 1997; 39: 175
|
| [14] | Parkins R N, O'Dell C S, Fessler R R. Corros Sci,1984; 24: 343
|
| [15] | Thomas J G N, Nurse T J, Walker R. Br Corros J,1970; 5: 87
|
| [16] | Cheng Y F, Niu L. Electrochem Commun, 2007; 9:558
|
| [17] | Liang P, Li X G, Du C W, Chen X. Mater Des, 2009;30: 1712
|
| [18] | Gu B, Luo J L, Mao X. Corrosion, 1999; 55: 96
|
| [19] | Cheng Y F. J Mater Sci, 2007; 42: 2701
|
| [20] | Eslami A, Fang B, Kania R, Worthingham B, Been J, Eadie R,Chen W. Corros Sci, 2010; 52: 3750
|
| [21] | Eslami A, Kania R, Worthingham B, Boven G V, Eadie R, ChenW. Corros Sci, 2011; 53: 2318
|
| [22] | Torres-Islas A, Gonzalez-Rodriguez J G, Uruchurtu J,Serna S. Corros Sci, 2008; 50: 2831
|
| [23] | Liu Z Y, Li X G, Du C W, Zhai G L, Cheng Y F.Corros Sci, 2008; 50: 2251
|
| [24] | Zhang L, Li X G, Du C W, Huang Y Z. Mater Des,2009; 30: 2259
|
| [25] | Xiao J, Wu M, Chen X, Wang C X. Mater HeatTreat, 2010; 39(18): 28
|
| [26] | Yan M C, Wang J Q, Han E H, Ke W. Corros Sci,2008; 50: 1331
|
| [27] | Li M C, Cheng Y F. Electrochim Acta, 2007; 52:8111
|
| [28] | Bouaeshi W, Ironside S, Eadie R. Corrosion, 2007;63: 648
|
| [29] | Beavers J A, Harle B A. J Offshore Mech Arctic Eng, 2001; 123: 147
|
| [30] | Liu Z Y, Li X G, Zhang Y R, Du C W, Zhai G L. Acta Metall Sin (Eng Lett), 2009; 22: 58
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|