金属学报  2014 

RE对过共晶Al-80%Si合金凝固特性的影响*

DOI: 10.3724/SP.J.1037.2013.00659, PP. 610-618

Keywords: Al-Si合金,初生Si,RE,过冷度,组织

Full-Text   Cite this paper   Add to My Lib

Abstract:

利用高速摄影仪和SEM研究了RE对Al-80%Si合金凝固过程中再辉界面形貌、初生Si形貌和凝固后组织的影响.结果发现,加入RE前后的Al-80%Si合金均存在2个临界过冷度DT1和DT2,在过冷度小于DT1时,初生Si的形貌为粗大的长片状,表面有明显的棱角;过冷度大于DT2后,合金在凝固过程中的再辉界面为平面状,凝固后的初生Si形貌为均匀、细小、表面有光滑凸起的球状,并且晶粒表面的棱角消失;当过冷度在DT1与DT2之间时,合金在凝固过程中的再辉界面为树枝状,凝固后的初生Si形貌部分为表面有棱角的片状和块状,部分为表面无棱角的球状.对于Al-80%Si合金而言,DT1和DT2分别约为132和250K.RE能降低Al-80%Si合金DT1和DT2的值,对于Al-80%Si-1%RE而言,DT1和DT2分别约为60和199K.

References

[1]  Xu C L, Wang H Y, Yang F Y, Jiang Q C. Mater Sci Eng, 2007; A452: 341
[2]  Zuo M, Liu X F, Sun Q Q, Jiang K. J Mater Process Technol, 2009; 209: 5504
[3]  Yu L N, Liu X F, Ding H M, Bian X F. J Alloys Compd, 2007; 432: 156
[4]  Zuo M, Zhao D G, Teng X Y, Geng H R, Zhang Z S. Mater Des, 2013; 47: 857
[5]  Wu Y P, Wang S J, Li H, Liu X F. J Alloys Compd, 2009; 477: 139
[6]  Shi W X, Gao B, Tu G F, Li S W, Hao Y, Yu F X. J Rare Earth, 2010; 28: 367
[7]  Chang J Y, Kim G H, Moon I G, Choi C S. Scr Mater, 1998; 39: 307
[8]  Chen C, Liu Z X, Ren B, Wang M X, Weng Y G, Liu Z Y. Trans Nonferrous Met Soc China, 2007; 17: 301
[9]  Li Q L, Xia T D, Lan Y F, Li P F, Fan L. Mater Sci Eng, 2013; A588: 97
[10]  Wei B K, Lin H T, Liu J M, Cai Q Z, Tong X L, Mao Y F. Spec Cast Nonferrous Alloys, 1993; (3): 6(魏伯康, 林汉同, 刘俊明, 蔡启舟, 童杏林, 毛玉凤. 特种铸造及有色合金, 1993; (3): 6)
[11]  Zuo M, Jiang K F, Liu X F. J Alloys Compd, 2010; 503: L26
[12]  Faraji M, Todd I, Jones H. J Mater Sci, 2005; 40: 6363
[13]  Jiang Q C, Xu C L, Lu M, Wang H Y. Mater Lett, 2005; 59: 624
[14]  Yi H, Zhang D. Mater Lett, 2003; 57: 2523
[15]  Ohmi T, Matsuura K, Kudoh M. J Jpn Inst Light Met, 1998; 48: 618
[16]  Jian Z Y, Zhu M, Jie W Q. Mater China, 2010; 29: 20(坚增运, 朱 满, 介万奇. 中国材料进展, 2010; 29: 20)
[17]  Hernandez F C R, Sokolowski J H. J Alloys Compd, 2006; 426: 205
[18]  Jin F W, Ren Z M, Ren W L, Deng K, Zhong Y B, Yu J B. Sci Technol Adv Mater, 2008; 9: 024202
[19]  Zhang Q, Liu X F, Dai H S. J Alloys Compd, 2009; 480: 376
[20]  Xu C L, Jiang Q C, Yang Y F, Wang H Y, Wang J G. J Alloys Compd, 2006; 422: L1
[21]  Shi W X, Gao B, Tu G F, Li S W. J Alloys Compd, 2010; 508: 480
[22]  Li Q L, Xia T D, Lan Y F, Zhao W J, Fan L, Li P F. J Alloys Compd, 2013; 562: 25
[23]  Jian Z Y, Nagashio K, Kuribayashi K. Metall Mater Trans, 2002; 33A: 2947
[24]  Jian Z Y, Kuribayashi K, Jie W Q, Chang F E. Acta Mater, 2006; 54: 3227
[25]  Liu R P, Volkmann T, Herlach D M. Acta Mater, 2001; 49: 439
[26]  Wang Q, Liu R P, Qian Y Q, Lou D C, Su Z B, Ma M Z, Wang W K, Panofen C, Herlach D M. Scr Mater, 2006; 54: 37
[27]  Lu S Z, Hellawell A. Metall Mater Trans, 1987; 18A: 1721
[28]  Jian Z Y, Yang X Q, Chang F E, Jie W Q. Metall Mater Trans, 2010; 41A: 1826
[29]  David R L. CRC Handbook of Chemistry and Physics. Tokyo: CRC Press, 1989: B2
[30]  Jian Z Y, Kuribayashi K, Jie W Q. Acta Mater, 2004; 52: 3323

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133