MOCVD方法在SrFe12O19表面生长Fe薄膜及其吸波性能
DOI: 10.11900/0412.1961.2013.00774, PP. 1095-1101
Keywords: 羰基铁,金属有机化学气相沉积,电磁,微波吸收
Abstract:
采用金属有机化学气相沉积(MOCVD)工艺,以高纯Fe(CO)5和SrFe12O19为原料,高纯N2为载气,在SrFe12O19表面沉积连续Fe膜,从而制得Fe-SrFe12O19复合材料.用XRD,SEM,EDS和矢量网络分析仪对粉末的结构及电磁性能进行表征并对其吸波性能进行研究.结果表明,SrFe12O19表面沉积的膜层为纯a-Fe相,厚度约为0.5mm,沉积薄膜比较均匀完整地覆盖在SrFe12O19表面.SrFe12O19表面沉积a-Fe膜后,其电磁性能发生明显改变,吸波性能有较好改善.沉积时间30min时制备的样品有最佳的吸波效果,涂层厚度为1.5~3.0mm时,最小反射率均低于-19dB,在6.8~18.0GHz均能实现吸波强度低于-10dB.随着厚度的增加,反射率峰值先减少后增加,厚度为2.0mm时,达到最小值-21.2dB.
| [1] | Huang Y B, Qian J S, Zhang J Y. J Chin Coal Soc, 2010; 35: 135 (黄煜镔, 钱觉时, 张建业. 煤炭学报, 2010; 35: 135)
|
| [2] | Hirata A, Morita M, Shiozawa T. IEEE Trans Electromagn, 2003; 45C: 109
|
| [3] | Liu Y, Liu X X, Wang X J, Zhang Z Y, Li R, Guo L. Chin J Nonferrous Met, 2013; 23: 168 (刘 渊, 刘祥萱, 王煊军, 张泽洋, 李 茸, 郭 磊. 中国有色金属学报, 2013; 23: 168)
|
| [4] | J, Wang W, Sun Z G, Gong J G. Acta Metall Sin, 2010; 46: 967 (周 静, 王 维, 孙志刚, 宫建国. 金属学报, 2010; 46: 967)
|
| [5] | Liu Y, Liu X X, Wang X J, Chen X. J Chin Ceram Soc, 2013; 41: 755 (刘 渊, 刘祥萱, 王煊军, 陈 鑫. 硅酸盐学报, 2013; 41: 755)
|
| [6] | Wang Y F, Li Q L, Zhang C R, Jing H X. J Alloys Compd, 2009; 467: 284
|
| [7] | Yao X B, Hu G G, Yin P, Fang Q Q, Lv Q R. Funct Mater, 2002; 33: 633 (姚学标, 胡国光, 尹 萍, 方庆清, 吕庆荣. 功能材料, 2002; 33: 633)
|
| [8] | Jing H X, Li Q L, Ye Y, Yang X F. Acta Mater Comp Sin, 2013; 30: 130 (景红霞, 李巧玲, 叶 云, 杨晓峰. 复合材料学报, 2013; 30: 130)
|
| [9] | Liu Y, Liu X X, Wang X J. J Alloys Compd, 2014; 584: 249
|
| [10] | Tong G X, Gong J G, Zhang W Y, Zhang W, Wang W, Dong D M. Acta Metall Sin, 2008; 44: 1001 (童国秀, 宫建国, 张五一, 张 巍, 王 维, 董德明. 金属学报, 2008; 44: 1001)
|
| [11] | Liu Y, Liu X X, Wang X J, Wen W. Chin Phys Lett, 2014; 31: 047702
|
| [12] | Cheng Y L, Dai J M, Wu Y P. J Magn Magn Mater, 2010; 32: 97
|
| [13] | Pan X F, Mu G H, Shen H G, Gu M Y. Appl Surf Sci, 2007; 253: 4119
|
| [14] | Pan X F, Shen H G, Qiu J X, Gu M Y. Mater Chem Phys, 2007; 101: 505
|
| [15] | Pan X F, Shen H G, Qiu J X, Gu M Y. J Mater Sci, 2007; 42: 2086
|
| [16] | Zhang Z Y, Liu X X, Wang X J, Wu Y P, Liu Y. J Magn Magn Mater, 2012; 324: 2177
|
| [17] | Zhang Z Y, Liu X X, Wang X J, Wu Y P, Rong L. J Alloys Compd, 2012; 525: 114
|
| [18] | Zhang S Y, Cao Q X. Mater Sci Eng, 2012; B177: 678
|
| [19] | Liu Y, Liu X X, Chen X, Wang X J. J Inorg Mater, 2013; 28: 1328 (刘 渊, 刘祥萱, 陈 鑫, 王煊军. 无机材料学报, 2013; 28: 1328)
|
| [20] | Yang Y, Xu C L, Xia Y X, Wang T, Li F S. J Alloys Compd, 2010; 493: 549
|
| [21] | Zhang B S, Feng Y, Xiong J, Yang Y, Lu H X. IEEE Trans Magn, 2006; 42: 1778
|
| [22] | Naito Y, Suetake K. IEEE Trans Microwave Theory Technol, 1971; 19: 65
|
| [23] | Meshram M R, Agrawal N K, Sinha B, Misra P S. J Magn Magn Mater, 2004; 271: 207
|
| [24] | Maeda T, Sugimoto S, Kagotani T, Tezuka N, Inomata K. J Magn Magn Mater, 2004; 281: 195
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|