多向压缩中AZ31镁合金变形行为的EBSD跟踪研究
DOI: 10.3724/SP.J.1037.2013.00112, PP. 932-938
Keywords: AZ31镁合金,拉伸孪生,退孪生,局部区域应变,EBSD跟踪研究
Abstract:
利用显微硬度点法结合电子背散射衍射(EBSD)技术,跟踪研究了多向压缩路径下AZ31镁合金的变形行为.采用先沿板材横向(TD)压缩然后沿板材法向(ND)进行压缩的应变路径.结果表明,绝大多数晶粒TD压缩变形中主要以{1012}拉伸孪生为主,ND压缩变形过程中主要以退孪生为主,少数晶粒变形行为不同的原因是由于其初始取向偏离基面织构太大.在ND压缩变形中发生退孪生行为的晶粒内,没有发现新的孪生变体出现,表明退孪生比激活一个新的孪生变体要容易.剩余孪晶面积分数减少到0时,ND压缩变形中的局部区域应变小于TD压缩变形,表明完全退孪生所需应变比孪生小.
| [1] | Lou X Y, Li M, Boger R K, Agnew S R, Wagoner R H.Int J Plast, 2007; 23: 44
|
| [2] | Liu Q. Acta Metall Sin, 2010; 46: 1458
|
| [3] | (刘庆. 金属学报, 2010; 46: 1458)
|
| [4] | Barnett M R. Mater Sci Eng, 2007; A464: 1
|
| [5] | Barnett M R. Mater Sci Eng, 2007; A464: 8
|
| [6] | Martin E, Capolungo L, Jiang L, Jonas J J. Acta Mater, 2010; 58: 3970
|
| [7] | Luo J R, Godfrey A, Liu W, Liu Q. Acta Mater, 2012;60: 1986
|
| [8] | Luo J R, Liu Q, Liu W, Godfrey A. Acta Metall Sin,2011; 47: 1567
|
| [9] | (罗晋如, 刘庆, 刘伟, Godfrey A. 金属学报, 2011; 47:1567)
|
| [10] | Luo J R, Liu Q, Liu W, Godfrey A. Acta Metall Sin,2012; 48: 717
|
| [11] | (罗晋如, 刘庆, 刘伟, Godfrey A. 金属学报, 2012; 48:717)
|
| [12] | Huang H T, Liu W, Godfrey A, Tang R H, Liu Q. Acta Metall Sin, 2012; 48: 357
|
| [13] | (黄洪涛, 刘伟, Godfrey A, 唐瑞鹤, 刘庆. 金属学报,2012; 48: 357)
|
| [14] | Wang Y N, Huang J C. Acta Mater, 2007; 55: 897
|
| [15] | Proust G, Tome C N, Jain A, Agnew S R. Int JPlast, 2009; 25: 861
|
| [16] | Chapelle D, Darrieulat M. Mater Sci Eng, 2003;A347: 32
|
| [17] | Lineau C, Rey C, deLesegno P V. Mater Sci Eng,1997; A234: 853
|
| [18] | Delaire F, Raphanel J L, Rey C. Acta Mater, 2000;48: 1075
|
| [19] | Barnett M R, Jacob S, Gerard B F, Mullins J G. Scr Mater, 2008; 59: 1035
|
| [20] | Allais L, Bornert M, Bretheau T, Caldemasion D.Acta Mater, 1994; 42: 3865
|
| [21] | Huang H T,PhD Dissertation, Tsinghua University,Beijing, 2013
|
| [22] | (黄洪涛. 清华大学博士学位论文, 北京, 2013)
|
| [23] | Huang H T, Godfrey A, Liu W, Tang R H, Liu Q. Acta Metall Sin, 2012; 48: 915 (黄洪涛, Godfrey A, 刘伟, 唐瑞鹤, 刘庆. 金属学报,2012; 48: 915)
|
| [24] | Nave M D, Barnett M R. Scr Mater, 2004; 51: 881
|
| [25] | Yang X Y, Zhang L. Acta Metall Sin, 2009; 45: 1303
|
| [26] | (杨续跃, 张雷. 金属学报, 2009; 45: 1303)
|
| [27] | Brown D W, Agnew S R, Bourke M A M, Holden T M, Vogel S C,Tome C N. Mater Sci Eng, 2005; A399: 1
|
| [28] | Clausen B, Tome C N, Brown D W, Agnew S R. Acta Mater, 2008; 56: 2456
|
| [29] | Lou C, Zhang X Y, Wang R H, Duan G L, Liu Q. Acta Metall Sin, 2013; 49: 291
|
| [30] | (娄超,张喜燕, 汪润红, 段高林, 刘庆.金属学报, 2013; 49: 291)
|
| [31] | Wu L, Agnew S R, Brown D W, Stoica G M, Clausen B, Jain A,Fielden D E, Liaw P K. Acta Mater, 2008; 56: 3699
|
| [32] | Wu L, Jain A, Brown D W, Stoica G M, Agnew S R, Clausen B,Fielden D E, Liaw P K. Acta Mater, 2008; 56: 688
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|