Fe－6.5%Si轧制板材热处理制度工艺的优化
DOI: 10.3724/SP.J.1037.2013.00520, PP. 1445-1451
Keywords: Fe－6.5%Si合金,热处理,塑性,硬度
Abstract:
研究了热轧Fe－6.5%Si(质量分数)高硅钢薄板在不同温度、不同时间的热处理条件下其组织及合金力学性能的变化.结果表明,经过热处理的试样具有更好的力学性能,300℃拉伸延伸率比热轧态试样的延伸率(9.09%)高出近1倍,硬度也大幅下降,有利于后续轧制的进行.通过对比分析,确定在850℃下保温1min并在盐水中淬火是较理想的热处理条件,在此条件下处理的Fe－6.5%Si合金板材组织均匀,塑性提高,硬度降低,有利于下一步轧制的进行,并且该条件也大大提高了现有的热处理效率,满足生产工艺的要求.
| [1] | Yelsukov Y P, Barinov V. Phys Met Metallogr, 1984; 55(2): 119
|
| [2] | Ros－Ya\nez T, Houbaert Y, Fischer O, Schneider J. J Mater Process Technol, 2003; 141: 132
|
| [3] | Fish G E, Chang C F, Bye R. J Appl Phys, 1988; 64: 5370
|
| [4] | Fujita K, Namikawa M, Takada Y. J Mater Sci Technol, 2000; 16: 137
|
| [5] | Takada Y, Abe M, Masuda S, Inagaki J. J Appl Phys, 1988; 64: 5367
|
| [6] | Li R, Shen Q, Zhang L M, Zhang T. J Magn Magn Mater, 2004; 281: 135
|
| [7] | Wang W F. Powder Metall, 1995; 38: 289
|
| [8] | Ros－Yanez T, Houbaert Y, Rodriguez V G. J Appl Phys, 2002; 91: 7857
|
| [9] | Barros J, Ros－Yanez T, Vandenbossche L, Dupre L, Melkebeek J,Houbaert Y. J Magn Magn Mater, 2005; 290－291: 1457
|
| [10] | Ishizaka T, Yamabe K, Takahashi T. J Jpn Inst Met, 1996; 30: 552
|
| [11] | Ros－Yanez T, Houbaert Y, Fischer O, Schneider J. IEEE Trans Magn, 2001; 37: 2321
|
| [12] | Liang Y F, Lin J P, Ye F, Wang Y L, Chen G L. Met Funct Mater, 2010; 17(2): 43
|
| [13] | (梁永锋, 林均品, 叶丰, 王艳丽, 陈国良. 金属功能材料, 2010; 17(2): 43)
|
| [14] | Lin J P, Ye F, Chen G L, Wang Y L, Liang Y F, Jin J N, Liu Y. Front Sci, 2007; 1(2): 13
|
| [15] | (林均品, 叶丰, 陈国良, 王艳丽, 梁永锋, 金吉男, 刘艳. 前沿科学, 2007; 1(2): 13)
|
| [16] | Liu Y, Liang Y F, Ye F, Lin J P, Chen G L. Spec Steel, 2007; 28(3): 28
|
| [17] | (刘艳, 梁永锋, 叶丰, 林均品, 陈国良. 特殊钢, 2007; 28(3): 28)
|
| [18] | Fang X S, Liang Y F, Ye F, Lin J P . J Appl Phys, 2012; 111: 0949139)
|
| [19] | Liang Y F. PhD Dissertation, University of Science and Technology Beijing, 2011
|
| [20] | (梁永锋. 北京科技大学博士学位论文, 2011)
|
| [21] | Liang Y F, Lin J P, Ye F, Wang Y L, Zhang L Q, Chen G L. Trans Mater Heat Treat, 2009; 30(2): 85
|
| [22] | (梁永锋, 林均品, 叶丰, 王艳丽, 张来启, 陈国良. 材料热处理学报, 2009; 30(2): 85)
|
| [23] | Shin J S, Bae J S, Kim H J, Lee H M, Lee T D, Lavernia E J, Lee Z H. Mater Sci Eng,2005; A407: 282
|
| [24] | Shin J S, Lee S M, Moon B M, Lee H M, Lee T D, Lee Z H. Met Mater Int, 2004; 10: 581
|
| [25] | Yu J H, Shin J S, Bae J S, Lee Z H, Lee T D, Lee H M, Lavernia E J.Mater Sci Eng, 2001; A307: 29
|
| [26] | Zhang Z H, Wang W P, Fu H D, Xie J X. Mater Sci Eng, 2011; A530: 519
|
| [27] | Witting J E, Frommeyer G. Metall Mater Trans, 2008; 39A: 252
|
| [28] | Bozorth R M. Ferromagnetism. New York: Van Nostrand Reinhold Company, 1951: 67
|
| [29] | He Z Z. Electrical Steel. Beijing: Metallurgical Industry Press, 1997: 594
|
| [30] | (何忠治. 电工钢. 北京: 冶金工业出版社, 1997: 594)
|
| [31] | Shin J S, Lee Z H, Lee T D, Lavernia E J. Scr Mater, 2001; 45: 725
|
| [32] | Raviprasad K, Chattopadhyay K. Acta Metall Mater, 1993; 41: 609
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|