冷坩埚定向凝固Ti44Al6Nb合金的组织演变规律
DOI: 10.3724/SP.J.1037.2013.00550, PP. 1356-1362
Keywords: Ti44Al6Nb合金,冷坩埚,定向凝固,微观组织
Abstract:
利用无污染的电磁冷坩埚进行定向凝固,对大尺寸Ti44Al6Nb(原子分数,%)定向合金锭进行研究,研究了抽拉速率和加热功率对合金表面质量、固/液界面形态、枝晶形态以及相选择的影响.结果表明,随抽拉速率降低和功率增大,铸锭表面质量提高,它们通过改变熔体过热度和糊状区体积而影响铸锭的表面质量;随抽拉速率增加,凝固界面变凹,且晶粒宽度变大,抽拉速率超过临界值后,柱状晶不能连续生长;随功率增加,晶粒宽度减小;在抽拉速率较低或功率较高时,易发生CET转变;抽拉速率为0.5mm/min时的初始凝固相为α相,其它抽拉速率下初始凝固相为β相.
| [1] | Saari H, Beddoes J, Seo D Y, Zhao L.Intermetallics, 2005; 13: 941
|
| [2] | Ding X F, Lin J P, Zhang L Q, Su Y Q, Chen G L.Acta Mater, 2012; 60: 498
|
| [3] | Liu D M, Li X Z, Su Y Q, Guo J J, Fu H Z.Intermetallics, 2011; 19: 175
|
| [4] | Blackburn M.Science, Techbology and Application of Titanium. London: Pergmin Press, 1970: 1
|
| [5] | Yamaguchi M, Johnson D R, Lee H N, Inui H.Intermetallics, 2000; 8: 511
|
| [6] | Murakami K, Fujiyama T, Koike A, Okamoto T. Acta Metall, 1983; 31: 1425
|
| [7] | Uhlmann D R, Seward T P, Chalmers B.Trans Metall Soc AIME, 1996; 236: 527
|
| [8] | Lin J P, Zhao L L, Li G Y, Zhang L Q, Song X P, Ye F, Chen G L.Intermetallics, 2011; 19: 131
|
| [9] | Yang X, Xi Z P, Liu Y, Tang H, Hu K, Jia W P. Trans Nonferrerous Met Soc China, 2012; 22: 2628
|
| [10] | Song L, Zhang L Q, Xu X J, Sun J, Lin J P.Scr Mater, 2013; 68: 929
|
| [11] | Wang G, Xu L, Wang Y, Zheng Z, Cui Y Y, Yang R.Acta Metall Sin, 2011; 47: 587
|
| [12] | (王刚, 徐磊, 王永, 郑卓, 崔玉友, 杨锐. 金属学报, 2011; 47: 587)
|
| [13] | Lin J P, Chen G L.Mater China, 2009; 28(1): 31
|
| [14] | (林均品, 陈国良. 中国材料进展, 2009; 28(1): 31)
|
| [15] | Huang X, Qi L C, Li Z X.Rare Met Mater Eng, 2006; 35: 1845
|
| [16] | (黄旭, 齐立春, 李臻熙. 稀有金属材料与工程, 2006; 35: 1845)
|
| [17] | Wang G, Zheng Z, Chang L T, Xu L, Cui Y Y, Yang R.Acta Metall Sin, 2011; 47: 1263
|
| [18] | (王刚, 郑卓, 常立涛, 徐磊, 崔玉友, 杨锐. 金属学报, 2011; 47: 1263)
|
| [19] | Huang X, Qi L C, Li Z X.Rare Met Mater Eng, 2006; 35: 1848
|
| [20] | (黄旭, 齐立春, 李臻熙. 稀有金属材料与工程, 2006; 35: 1848)
|
| [21] | Kartavykh A V, Tcherdyntsev V V, Zollinger J.Mater Chem Phys, 2010; 119: 347
|
| [22] | Zhang H R, Gao M, Tang X X, Zhang H.Acta Metall Sin, 2010; 46: 890
|
| [23] | (张花蕊, 高明, 唐晓霞, 张虎. 金属学报, 2010; 46: 890)
|
| [24] | Luo W Z, Shen J, Min Z X, Fu H Z.Rare Met Mater Eng, 2009; 38: 1442
|
| [25] | (罗文忠, 沈军, 闵志先, 傅恒志. 稀有金属材料与工程, 2009; 38: 1442)
|
| [26] | Yang J R, Chen R R, Ding H S, Guo J J, Su Y Q, Fu H Z.J Mater Process Technol, 2013; 213: 1355
|
| [27] | Yang J R, Chen R R, Ding H S, Guo J J, Han J C, Fu H Z.Intermetallics, 2013; 42: 184
|
| [28] | Ding H S, G J J, Chen R R, Fu H Z.Mater China, 2010; 29(2): 14
|
| [29] | (丁宏升, 郭景杰, 陈瑞润, 傅恒志. 中国材料进展, 2010; 29(2): 14)
|
| [30] | Xiao Z X, Zheng L J, Yang L L, Yan J, Zhang H.Acta Metall Sin, 2010; 46: 1223
|
| [31] | (肖志霞, 郑立静, 杨莉莉, 闫洁, 张虎. 金属学报, 2010; 46: 1223)
|
| [32] | Ding X F, Lin J P, Zhang L Q, Wang H L, Hao G J, Chen G L.J Alloys Compd, 2010; 506: 117
|
| [33] | Fu H Z, Guo J J, Su Y Q, Liu L, Xu D M, Li J S.Chin JNonferrous Met, 2003; 13: 797
|
| [34] | (傅恒志, 郭景杰, 苏彦庆, 刘林, 徐达鸣, 李金山. 中国有色金属学报, 2003; 13: 797)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|