C对单晶高温合金持久性能的影响*
DOI: 10.3724/SP.J.1037.2013.00790, PP. 854-862
Keywords: C,单晶高温合金,微观组织,持久寿命
Abstract:
研究了5种不同含量的C对单晶高温合金凝固组织及持久性能的影响.结果表明,随着C含量的增加,共晶数量明显减少,碳化物数量增多,且碳化物主要分布在枝晶间区域,当C含量较高时,在枝晶干上也有少量碳化物出现.经过热处理后,合金的枝晶间粗大的g/g′共晶基本消除,枝晶间少量未被固溶掉的g/g′共晶,达到了较好的均匀化效果;碳化物形貌比铸态更为简单,尺寸明显减小,体积分数减小,且分布更加弥散,碳化物类型更加丰富,出现了粒状和链状的M23C6碳化物.随C含量增加合金的高温持久寿命先增大后减小,当C含量为0.045%时,高温持久寿命最大.引起持久性能变化的主要原因是由于合金中未消除的共晶、碳化物及缩松的存在,未消除的共晶以及碳化物都是裂纹萌生的位置,而共晶和碳化物的数量随着C含量的增大又呈相反的变化趋势,因此C的加入要适量.
| [1] | Yu Z H, Liu L, Zhao X B, Zhang W G, Zhang J, Fu H Z. China Foundry, 2010; 7: 352
|
| [2] | Qin X Z, Guo J T, Yuan C, Hou J S, Ye H Q. Mater Lett, 2008; 62: 258
|
| [3] | Wasson A J, Fuchs G E. Mater Charact, 2012; 74: 11
|
| [4] | Sun X T. Master Thesis, Shenyang University of Technology, 2007(孙新涛. 沈阳工业大学硕士学位论文, 2007)
|
| [5] | Wagner A, Shollock B A, Mclean M. Mater Sci Eng, 2004; A374: 270
|
| [6] | Guo J T. Acta Metall Sin, 2010; 46: 513(郭建亭. 金属学报, 2010; 46: 513)
|
| [7] | Pollock T M, Murphy W H, Goldman W H, Antolokch S D, Stusrud R W, MacKay R A. Superalloys 1992, Warrendale: TMS, 1992: 125
|
| [8] | Liu G, Liu L, Zhang S X, Yang C B, Zhang J, Fu H Z. Acta Metall Sin, 2012; 48: 845(刘 刚, 刘 林, 张盛霞, 杨初斌, 张 军, 傅恒志. 金属学报, 2012; 48: 845)
|
| [9] | Wilson B C, Cutler E R, Fuchs G E. Mater Sci Eng, 2008; A479: 356
|
| [10] | Zhang Z, Lou L. J Mater Sci Technol, 2007; 23: 289
|
| [11] | Liu L, Huang T W, Zhang J, Fu H Z. Mater Lett, 2007; 61: 227
|
| [12] | Al-Jarba K A, Fuchs G E. JOM, 2004; (9): 50
|
| [13] | Tin S, Pollock T M, King W T. Superalloys 2000, Boston: TMS, 2000: 201
|
| [14] | Wasson A J, Fuchs G E. Mater Charact, 2012; 74: 11
|
| [15] | Tin S, Pollock T M. Mater Sci Eng, 2003; A348: 111
|
| [16] | Al-Jarba K A, Fuchs G E. Mater Sci Eng, 2004; A373: 255
|
| [17] | Liu L R, Jin T, Zhao N R, Wang Z H, Sun X F, Guan H R, Hu Z Q. Mater Lett, 2004; 58: 2290
|
| [18] | Cutler E R, Wasson A J, Fuchs G E. Scr Mater, 2008; 58: 146
|
| [19] | Liu L R, Jin T, Zhao N R, Sun X F, Guan H R, Hu Z Q. Mater Sci Eng, 2003; A361: 191
|
| [20] | Liu L R, Jin T, Zhao N R, Wang Z H, Sun X F, Guan H R, Hu Z Q. Mater Sci Eng, 2004; A385: 105
|
| [21] | Yu J J, Sun X F, Zhao N R, Jin T, Guan H R, Hu Z Q. Trans Nonferrous Met Soc China, 2006; 16: 1973
|
| [22] | Xiao L, Chen D L, Chaturvedi M C. Mater Sci Eng, 2006; A437: 157
|
| [23] | Zhou Y Z, Volek A. Mater Sci Eng, 2008; A479: 324
|
| [24] | Glas R, Jouiad M, Caron P. Acta Mater, 1996; 44: 4917
|
| [25] | Kamaraj M. Sadhana, 2003; 28: 115
|
| [26] | Raffaitin A, Monceau D, Andrieu E. Acta Mater, 2006; 54: 4473
|
| [27] | Kim I S, Cho B G, Seo S M. Mater Lett, 2008; 62: 1110
|
| [28] | Yu Z H. PhD Dissertation, Northwestern Polytechnical University, Xi′an, 2011(余竹焕. 西北工业大学博士学位论文, 西安, 2011)
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|