金属学报  2014 

过冷Fe82B17Si1合金的再辉效应模拟及组织演化*

DOI: 10.3724/SP.J.1037.2013.00813, PP. 795-801

Keywords: Fe82B17Si1合金,JMAK模型,过冷,共晶组织

Full-Text   Cite this paper   Add to My Lib

Abstract:

通过熔融玻璃净化与循环过热相结合的方法获得过冷度ΔT=6~280K范围内的Fe82B17Si1共晶合金的凝固组织演变;结合突变方程和JMAK模型拟合凝固过程的冷却曲线,拟合结果符合Fe82B17Si1共晶合金的组织类型及形态随过冷度的变化规律.结果表明,当6K≤ΔT250K时,凝固组织为完全非规则共晶组织.

References

[1]  Schroers J, Holland-Moritz D, Herlach D M. Mater Sci Eng, 1997; A226-228: 990
[2]  Luborsky F E. Amorphous Metallic Alloys. London: Butterworth & Co., 1983: 381
[3]  Zhang Z Z. PhD Dissertation, Northwestern Polytechnical University, Xi′an, 1993(张振忠. 西北工业大学博士学位论文, 西安, 1993)
[4]  Saleh A M, Clemente R A. J Appl Phys, 2004; 43: 3624
[5]  Emadi D, Whiting L, Djurdjevic M, Kierkus W T, Sokolowski J. MJoM, 2004; 10: 91
[6]  Gandin Ch-A, Mosbah S, Volkmann Th, Herlach D M. Acta Mater, 2008; 56: 3023
[7]  Yang W, Liu F, Liu H, Wang H F, Yang G C, Zhou Y H. J Cryst Growth, 2009; 311: 3225
[8]  Liu F, Sommer F, Mittemeijer E J. J Mater Sci, 2004; 39: 1621
[9]  Xu J F, Liu F, Zhang K, Gong M M. Mater Sci Technol, 2012; 28: 274
[10]  Christian J W. The Theory of Transformation in Metals and Alloys. OXford: Pergamon Press, 2002: 623
[11]  Xu J F, Liu F, Zhang K, Gong M M. Mater Sci Technol, 2012; 28: 274
[12]  Yang C L, Yang G C, Lu Y P, Chen J Q, Zhou Y H. Acta Metall Sin, 2005; 41: 1053(杨长林, 杨根仓, 卢一平, 陈甲琪, 周尧和. 金属学报, 2005; 41: 1053)
[13]  Goetzinger R, Barth M, Herlach D M. J Appl Phys, 1998; 84: 1643
[14]  Leonhardt M, Loser W, Lindenkreuz H G. Mater Sci Eng, 1999; A271: 31
[15]  Lu Y P, Yang G C, Xi Z Z, Wang H P, Zhou Y H. Mater Lett, 2005; 59: 1558
[16]  Lu Y P, Yang G C, Liu F, Wang H P, Zhou Y H. Mater Lett, 2007; 61: 987
[17]  Merz G D, Kattamis T Z. Metall Trans, 1977; 8A: 295
[18]  Croker M N, Fidler R S, Smith R W. Proc Roy Soc Lond, 1973; 335A: 15
[19]  Lu Y P, Yang G C, Liu F, Wang H P, Zhou Y H. Eur Phys Lett, 2006; 74: 281
[20]  Lu Y P, Liu F, Yang G C, Yang C L, Zhou Y H. Appl Phys Lett, 2006; 89: 241902
[21]  Wei B, Yang G C, Zhou Y H. Acta Metall, 1991; 39: 1249
[22]  Chu M G, Shionara Y, Flemings M C. Metall Trans, 1984; 15A: 1303
[23]  Murty Y, Kattamis T Z. J Cryst Growth, 1974; 22: 219
[24]  Wang H P, Yao W J, Wei B. Appl Phys Lett, 2006; 89: 201905
[25]  Bottinger W J, Aziz M J. Acta Metall, 1989; 37: 3379
[26]  Battezzati L, Antonione C, Baricco M. J Alloys Compd, 1997; 247: 164
[27]  Loser W, Hermann R, Leonhardt R. Mater Sci Eng, 1997; A224: 53
[28]  Lu Y P, Yang G C, Yang C L,Wang H P, Zhou Y H. Progress Nat Sci, 2006; 16: 287
[29]  Duhaj P, ?vec P. Mater Sci Eng, 1997; A226-228: 245
[30]  Valiev R Z, Korasilnikov N A, Tzenev N K. Mater Sci Eng, 1991; A137: 35
[31]  Zhang Z Z, Song G S, Yang G C. Progress Nat Sci, 2000; 10: 560(张振忠, 宋广生, 杨根仓. 自然科学进展, 2000; 10: 560)
[32]  Fras E, Lopez H F. Metall Mater Trans, 1999; 30B: 927
[33]  Saleh A M, Clemente R A. J Appl Phys, 2004; 43: 3624
[34]  Raghavan V. Phase Diagrams of Ternary Iron Alloys Part 6A. New Delhi: Electronic Publishing Center, Green Park Extension. 1993: 11, 406
[35]  Boettinger W J, Coriell S R, Trivedi R. Principles Technol, 1988; (IV): 13

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133