隔膜和熔融碳酸盐燃料电池(MCFCS)性能的研究(英文)
, PP. 109-119
Keywords: 电池隔膜,补偿隔膜收缩,带铸法,MCFC性能
Abstract:
用γLiAO2粉料和带铸法制备电池隔膜。隔膜有很高的阻窜能力和较低的欧姆极化。在电流密度为200和246mA/cm2下放电时,用此膜组装的电池组(三对电池,电极面积为122cm2)输出电压分别为2.01和1.78V,输出功率达53.4W.于200和300mA/cm2下放电时,单电池(电极面积为28cm2)输出电压分别高于0.85和0.75V,输出功率约6.6W.补偿隔膜收缩导致电池性能的提高.
| [1] | BohmeO . ,LeidichF .U . ,SalgeH .J .etal.Developmentofmaterialsandproductiontechnologiesformoltencarbonatefuelcells[J].Int .J .HydrogenEnergy ,1994 ,19(4 ) :349 355.
|
| [2] | MasonDM ,VandvunanJ .Productionofβ LiAO2 [D].USAPat:3998939,1976 .
|
| [3] | [2 ] KinositaK .,AckermanJ .P .ElectrolyteforUseinfuelcell[D].USAPat :4 1156 32 ,1978.
|
| [4] | BaumgartnerC .E .,DecarloV .J .,GluglaP .G .,etal.Moltencarbonatefuelcellelectrolytestructurefabri cationusingelectrophoreticdeposition[J].J.Electrochem .Soc .,1985,132 :57.
|
| [5] | [4 ] GeneralElectricCompany ,DOEcontractDEAC 0 2 80ET170 19[R].QuarterlyReport,1980 .
|
| [6] | LiNaichao ,YiBaolian ,KongLianying ,etal.Cold roll milledelectrolytemembraneformoltencarbonatefu elcells[J].MembraneScienceandTechnology (China) ,1997,17(2 ) :2 4 2 9.
|
| [7] | [6 ] LacovangeloC .D ,PascoW .D .Hot roll milledelectrolytestructureformoltencarbonatefuelcell[J].J .Electrochem .Soc.1988,135:2 2 1.
|
| [8] | UnitedTechnologiesCorporation .DOEContractDEACO1 79ET1544 0 [R].QuarterlyReportNo .4July Sept .1980 .
|
| [9] | InstituteofGasTechnology .EPRIContractNorp 10 85 10Project 4 0 2 2 7[R].January 1984 .
|
| [10] | LinHuaxin ,ZhangEnjun ,KongLianying ,etal.Studyofmoltencarbonatefuelcellperformance[J].Bat teryBimonthly(inChinese) ,1997,2 7(3) :110 113.
|
| [11] | [10 ] LinHuaxin ,YiBaolian ,LiNaichao ,etal.ThestudyonthePerformanceofMCFCmatrixpreparedbyflowcast[J].Electrochemistry(inChinese) ,1998,4 (4 ) :4 0 6～ 4 13.
|
| [12] | ArendtR .H .andCurranM .J.Alternatesynthesisofelectrolytematrixformoltencarbonatefuelcell[J].J .Electrochem .Soc .1980 ,12 7:16 6 0 16 6 6 .
|
| [13] | [12 ] LinHuaxin ,YiBaolian ,LiNaichao ,etal.Themothodofpreparingmatrixformoltencarbonatefuelcell[P].ChinaPatent :ApplicationNumber :971110 2 8.2 .
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|