静磁场对硫酸盐还原菌生物膜形成过程的影响
DOI: 10.11903/1002.6495.2013.327
Keywords: 硫酸盐还原菌 ,(SRB) ,生物膜 ,静磁场 ,吸附
Abstract:
采用铂片微排电极研究了硫酸盐还原菌(SRB)生物膜在有无磁场环境下的电化学行为。结果表明无磁场下铂片电极表面覆盖一层很厚的生物膜，通过显微镜观察厚度为141.4μm，生物膜电阻较大，生物膜脱吸附过程进行时间较长，生成的腐蚀性产物较多。磁场存在下SRB细菌不容易在铂片电极表面吸附，进而形成的生物膜较薄(厚度为67.06μm)，生物膜在很短时间内达到了脱吸附平衡状态，从而生物膜内腐蚀性物质较少，对基体的腐蚀作用较弱。电荷传质电阻Rct表明，磁场的引入极大地阻碍了电极表面电荷的运动，从而影响了电化学过程的顺利进行。
References
[1] Beech I B, Sunner J A, Hiraoka K. Microbe-surface interactions?in?biofouling and biocorrosion processes [J]. Int. Microbiol., 2005, 8: 157 [2] Muthukumar N, Maruthamuthu S, Palaniswamy N. Water-soluble inhibitor on microbiologically influenced corrosion in diesel pipeline [J]. Colloids Surf., 2006, 53(2): 260 [3] Videla H A. Prevention and control of biocorrosion [J]. Int. Biodeter. Biodegrada., 2002, 49: 259 [4] Videla H A, Herrera L K. Microbiologically influence corrosion: Looking to the future [J]. Int. Microbiol., 2005, 8: 169 [5] 刘慧娜, 孙吉慧, 沈加艳. 给水管网中管壁生物膜对水质二次污染的影响 [J]. 环保科技, 2009, 15(4): 9 [6] 叶琴, 李克娟, 郭佩佩等. 油田污水中碳钢表面生物膜生长规律及腐蚀电化学行为 [J]. 腐蚀科学与防护技术, 2013, 25(3): 195 [7] 李进, 许兆义, 李久义等. 再生水环境中304不锈钢生物膜腐蚀电化学特征 [J]. 物理化学学报, 2010, 26(10): 2638 [8] 刘宏芳, 黄玲, 刘涛等. 新型季鳞盐抗菌剂的合成及抗菌性能研究[J]. 腐蚀科学与防护技术, 2009, 21(3): 316 [9] Xu D, Li Y, Gu T. A synergistic d-tyrosine and tetrakis hydroxymethyl phosphonium sulfate biocide combination for the mitigation of an SRB biofilm [J]. World J. Microbiolo. Biotechnol., 2012, 28(10): 3067 [10] 刘宏芳, 黄玲, 刘涛等. 硫酸盐还原菌杀菌剂应用现状及研究进展 [J]. 中国腐蚀与防护学报, 2009, 29(2): 154 [11] Sorensen P A, Kill S, Dam-Johansen K. Anticorrosive coatings: a review [J]. Technol. Res., 2009, 6(2): 135 [12] Chico B, Simancas J, Vega J M, et al. Anticorrosive behaviour of alkyd paints formulated with ion-exchange pigments [J]. Prog.Org. Coat., 2008, 61(2-4): 283 [13] Ji W, Huang H, Deng A, et al. Effects of static magnetic fields on Escherichia coli [J]. Micron, 2009, 40(8): 894 [14] 智丽媛, 杜丽. 静磁场的细胞生物学效应的研究 [J]. 广东牙病防治, 2008, 7(16): 650 [15] Liu H F, Huang L, Zheng J S. Specification of sulfate reducing bacteria biofilms accumulation effects on corrosion initiation [J]. Mater. Corros., 2007, 58(1): 45 [16] Liu T, Liu H, Hu Y, et al. Growth characteristics of thermophile Sulfate-reducing bacteria and its effect on carbon steel [J]. Mater. Corros., 2009, 60(3): 218
Full-Text
Contact Us
service@oalib.com
QQ:3279437679
WhatsApp +8615387084133