硼-硫酸-草酸电解液降压阳极氧化疏孔膜层制备及表征

DOI: 10.11903/1002.6495.2013.116, PP. 154-158

Keywords: 2024铝合金,阳极氧化,降压,耐蚀性

Full-Text   Cite this paper   Add to My Lib

Abstract:

使用铝合金在硼-硫酸-草酸电解液中阳极氧化制备有序多孔层。初步探讨了恒流和降压阳极氧化过程膜层生长机理,采用扫描电镜(SEM)观察膜层微观形貌,结合电化学阻抗和动电位极化曲线研究不同阳极化工艺制备膜层试样在3.5%NaCl溶液中的耐蚀行为。结果表明,采用三段变压方式制备的阳极氧化膜表面孔密度降低,孔壁增厚,孔径为10~13nm。疏孔膜层的电化学行为表明孔壁及膜层厚度增大能提高试样电荷传递电阻和耐蚀性能。

References

[1]  Furneaux R C, Rigby W R, Davidson A P. The formation of controlled-porosity membranes from anodically oxidized aluminium[J]. Nature, 1989, 337: 147
[2]  Jamaati R, Toroghinejad M R. Microstructure and mechanical properties of Al/Al2O3 MMC produced by anodising and cold roll bonding [J]. Mater. Sci. Technol., 2011, 27(11): 1648
[3]  Jagminas, ce?ūniene A, Vrublevsky I, et al. Behavior of alumina barrier layer in the supporting electrolytes for deposition of nanowired materials [J]. Electrochim. Acta, 2010, 55(9): 3361
[4]  Bocchetta P, Sunseri C. Influence of initial treatments of aluminium on the morphological features of electrochemically formed alumina membranes [J]. Mater. Sci. Eng., 2003, 23C(6-8): 1021
[5]  Gao T, Meng G W. Template synthesis of single-crystal Cu nanowire arrays by electrodeposition [J]. Appl. Phys., 2001, 73A(2):251
[6]  Peng X S, Zhang J. Synthesis of highly ordered CdSe nanowire arrays embedded in anodic alumina membrane by electrodeposition in ammonia alkaline solution [J]. Phys. Lett., 2001, 343(5/6): 470
[7]  杨萍, 黎学明, 宗庆彬等. 电力系统用LF21铝合金的电化学腐蚀行为 [J]. 腐蚀科学与防护技术, 2012, 24(4): 309
[8]  Barbosa B A R S, Tavares S S M, Cobuc A, et al. Influence of microstructure on pitting corrosion resistance of alloy 904L superaustenitic stainless steel [J]. Corrosion, 2012, 68(8): 739
[9]  Zhang R, Jiang K M, Ding G Q. Surface morphology control on porous anodic alumina in phosphoric acid [J]. Thin Solid Films, 2010, 518(14): 3797
[10]  王美娟, 王日初, 彭超群等. 镁合金阳极氧化研究进展 [J]. 腐蚀科学与防护技术, 2012, 24(6): 508
[11]  徐源, Thompson G E, Wood G C. 多孔型铝阳极氧化膜孔洞形成过程的研究 [J]. 中国腐蚀与防护学报, 1989, 9(1): 1
[12]  Oh J H, Carl V T. The role of electric field in pore formation during aluminum anodization [J]. Electrochim. Acta, 2011, 56(11): 4044

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133