静高压下非晶(Fe0.99,Mo0.01)78Si9B13合金晶化过程的热力学研究
DOI: 10.11858/gywlxb.1997.04.005, PP. 260-265
Keywords: 高压,晶化,相变
Abstract:
在600~930K，常压到7GPa的范围内，对非晶(Fe0.99,Mo0.01)78Si9B13合金等温等压退火30min。实验表明：其晶化产物α-Fe(Mo,Si)、Fe3B和Fe2B相的析出与所加压力密切相关。压力使非晶(Fe0.99,Mo0.01)78Si9B13合金的晶化温度和亚稳Fe3B相的析出温度下降，在一定的压力和温度下，亚稳Fe3B相将向稳定Fe2B相转变，其转变温度随压力而变化。还对非晶(Fe0.99,Mo0.01)78Si9B13合金的晶化和亚稳Fe3B到稳定Fe2B转变的热力学机制进行了讨论，并给出Fe3B向Fe2B的相转变方程。
| [1] | Sakka S, Mackenzie L D. J Non-Cryst Solids, 1969, 1: 143.
|
| [2] | Iwasaki H, Masumoto T. J Mater Sci, 1988, 13: 2171.
|
| [3] | Wang W K, Iwasaki H, Fwkamachi K. J Mater Sci, 1980, 15: 2701.
|
| [4] | Koster U, Abel R, Balnke H. Glastechnische Berichte, 1983, 56: 584.
|
| [5] | Liu X D, Wang J T, Ding B Z. Scr Met Mater, 1993: 28-59.
|
| [6] | Wang W K, Iwasaki H. J Mater Sci, 1983, 18: 3765.
|
| [7] | Chen H S. J Chem Phys, 1968, 48: 2560.
|
| [8] | Guo Y C. Amorphous State Physics. Beijing: Scientific Press, 1984.
|
| [9] | Wu C T. J Non-Cryst Solids, 1974, 18: 21.
|
| [10] | Shimonura U. Phil Mag, 1974, 29: 547.
|
| [11] | Wang W K, Iwasaki H. J Mater Sci, 1982, 17: 1523.
|
| [12] | Iwasaki H, Wang W K, Endo S. Solid State Commun, 1982, 42: 380.
|
| [13] | Iwasaki H. Sci Rep RITU A, 1993, 31: 1.
|
Full-Text
|
|
Contact Us
service@oalib.com QQ:3279437679 
WhatsApp +8615387084133
|
|