层间颗粒增韧复合材料层压板的损伤阻抗特性

, PP. 116-120

Keywords: 复合材料层压板,层间颗粒增韧,损伤阻抗,准静压痕试验,增韧机理

Full-Text   Cite this paper   Add to My Lib

Abstract:

采用热塑性颗粒对HT7/5228、HT3/NY9200G和HT3/5224三种高温固化环氧基体复合材料层压板进行层间增韧。为了提高冲击后压缩强度(CAI)和考察损伤阻抗,测试了平均分层起始能量eⅡc以及接触力-凹坑深度关系。试验结果表明,增韧颗粒和基体树脂形成的层间区域能有效地吸收断裂能量并抑制分层的发生,eⅡc显著提高。在静压痕力下,层间增韧复合材料层压板具有较深的凹坑深度和较小的损伤面积。层间增韧的几何效应、裂纹传播路径控制、颗粒桥联以及裂尖屏蔽是主要的增韧机理,颗粒的塑性变形和最终失效也耗散了大量断裂能量。

References

[1]  [R] . NASA/ TP-2000-210481. Springfield : NASA , 2000.
[2]  Yang X , Shen Z , Yan Y, et al . New met hodology for evaluation toughness of composite laminates-investigation of damage resistance [J] . Chinese J ournal of Aeronautics , 2003 ,16 (2) : 73 - 79.
[3]  Pearson R A. Toughening Epoxies Using Rigid Thermoplastic Particles [A] . In : Keit h C R , Antony J K, eds. Toughened Plastics Ⅰ [C] . Washington D C: American ChemicalSociety , 1993.
[4]  Odagiri N , Muraki T , Tobukuro K. Toughness improvedhigh performance torayca prepreg T800H/ 3900 series [A] .In : Gilberto C E D , Newell W D , Brown P P , eds. Proceedings 33rd International SAMPE Symposium [C] . Covina ,CA : Society for t he Advancement of Material and ProcessEngineering , 1988. 272 - 283.
[5]  Odagiri N , Kishi H , Nakae H. T800H/ 3900-2 toughenedepoxy prepreg system: Toughening concept and mechanism[A] . In : Proc of t he 6t h Conf of t he American Society forComposites [C] . New Yoke : America Society for Composite , 1991. 43 - 52.
[6]  Groleau M R , Shi Y B , Yee A F , et al . Mode Ⅱ f racture ofcomposites interlayered wit h nylon particles [J] . CompositesScience and Technology , 1996 , 56 (11) : 1223 - 1240.
[7]  Sue H J , Jones R E , Garcia-Meitin E I. Fracture behaviourof toughened composites under mode Ⅰ and mode Ⅱ delamination [J] . J ournal of Materials Science , 1993 , 28 : 6381- 6391.
[8]  Volker A , Dale G, Michael S. Interlaminar crack growt h int hird-generation t hermoset prepreg system [J] . Pol ymer ,1993 , 34 (4) : 907 - 909.
[9]  National Materials Advisory Board. New Materials for Next-Generation Commercial Transport [M] . Washington D C:National Academy Press , 1996. 38.
[10]  Greenhalgh E S , Hiley M J . The assessment of novel materials and processes for t he impact tolerant design of stiffenedcomposite aerospace st ructures [J] . Composi tes Part A ,2003 , 34 (2) : 151 - 161.
[11]  Net tles A T , Douglas M J . A comparison of quasi-staticindentation to low-velocity impact
[12]  ASTM D6264298. Standard test met hod for measuring t hedamage resistance of a fiber-reinforced polymer-mat rix composite to a concent rated quasi-static indentation force [S] .
[13]  张彦中, 宁荣昌. 复合材料层合板抗冲击损伤的参数表征[J] . 航空材料学报, 1995 , 15 (1) : 56 - 62.Zhang Y Z , Ning R C. The characterizing parameters of impact resistance damage composite laminates [J] . J ournal ofAeronautical Materials , 1995 , 15 (1) : 56 - 62.
[14]  Duarte A , Herszberg I , Paton R. Impact resistance andtolerance of interleaved tape laminates [J] . CompositeS t ructure , 1999 , 47 (1 - 4) : 753 - 758.
[15]  Kageyama K, Kimpara I , Ohsawa I , et al . Mode Ⅰand modeⅡ delamination growt h of interlayer toughened carbon/ epoxy( T800H/ 3900-2) composite system [A] . In : Martin R H ,ed. Composite Materials : Fatigue and Fracture [C] . Philadelphia : American Society for Testing and Materials , 1995.19 - 37.
[16]  Dejan S. Delamination properties of a vinyl-ester/ glass fibrecomposite toughened by particulate-modified interlayers[D] . Canberra : Department of Engineering , Aust ralian National University , 2001.

Full-Text

Contact Us

service@oalib.com

QQ:3279437679

WhatsApp +8615387084133