We report on investigation the potential of a 7 wt% (8.35 × 10 20 Tm 3+/cm 3) doped silicate fibers for high-gain fiber amplifiers. Such a high ion concentration significantly reduces the required fiber length of high-power 2 μm fiber laser systems and allows the high-repetition rate operation in 2 μm mode-locked fiber lasers. To evaluate the feasibility of extracting high gain-per-unit-length from this gain medium, we measure several key material properties of the silicate fiber, including the absorption/emission cross-sections, upper-state lifetime, fiber background loss, and photodarkening resistance. We show through numerical simulations that a signal gain-per-unit-length of 3.78 dB/cm at 1950 nm can be achieved in a watt-level core-pumped Tm 3+-doped silicate fiber amplifier. In addition, an 18-dB 2013-nm amplifier is demonstrated in a 50-cm 7 wt% Tm 3+-doped double-clad silicate fiber. Finally, we experimentally confirm that the reported silicate host exhibits no observable photodarkening.
References
[1]
Clarkson, W.A.; Pearson, L.; Zhang, Z.; Kim, J.W.; Shen, D.; Boyland, A.J.; Sahu, J.K.; Ibsen, M. High Power Thulium-Doped Fiber Lasers. In Proceedings of Optical Fiber Communication Conference (OFC), San Diego, CA, USA, 22–26 March 2009; pp. 100–110.
Geng, J.; Wang, Q.; Luo, T.; Jiang, S.; Amzajerdian, F. Single-frequency narrow-linewidth Tm-doped fiber laser using silicate glass fiber. Opt. Lett. 2009, 34, 3493–3495, doi:10.1364/OL.34.003493.
[5]
Geng, J.; Wang, Q.; Smith, J.; Luo, T.; Amzajerdian, F.; Jiang, S. All-fiber Q-switched single-frequency Tm-doped laser near 2 μm. Opt. Lett. 2009, 34, 3713–3715, doi:10.1364/OL.34.003713.
[6]
Wang, Q.; Geng, J.; Luo, T.; Jiang, S. Mode-locked 2 μm laser with highly thulium-doped silicate fiber. Opt. Lett. 2009, 34, 3616–3618, doi:10.1364/OL.34.003616.
[7]
McCumber, D.E. Theory of phonon terminated optical masers. Phys. Rev. Lett. 1964, 134, A299–A306.
[8]
Digonnet, M.J.F.; Murphy-Chutorian, E.; Falquier, D.G. Fundamental limitations of the McCumber relation applied to Er-doped silica and other amorphous-host lasers. IEEE J. Quantum Electron. 2002, 38, 1629–1637, doi:10.1109/JQE.2002.805111.
[9]
Gorjan, M.; North, T.; Rochette, M. Model of the amplified spontaneous emission generation in thulium-doped silica fibers. J. Opt. Soc. Am. B. 2012, 29, 2886–2890, doi:10.1364/JOSAB.29.002886.
[10]
LIEKKI？ Application Designer v4.0. Available online: http://www.nlight.net/download/lad (accessed on 28 November 2013).
[11]
Nufern Tm3+-doped fibers. Available online: http://www.nufern.com. (accessed on 28 November 2013).
[12]
Engelbrecht, M.; Haxsen, F.; Wandt, D.; Kracht, D. Wavelength resolved intracavity measurement of the cross sections of a Tm-doped fiber. Opt. Express 2012, 16, 1610–1615, doi:10.1364/OE.16.001610.
[13]
Frith, G.; Carter, A.; Samson, B.; Faroni, J.; Farley, K.; Tankala, K.; Town, G.E. Mitigation of photodegradation in 790nm-pumped Tm-doped fibers. Proc. SPIE 2010, 7580, doi:10.1117/12.846230.
[14]
Koponen, J.J.; S？derlund, M.J.; Hoffman, H.J.; Tammela, S.K.T.; Po, H. Photodarkening in ytterbium-doped silica fibers. Proc. SPIE 2005, 5990, doi:10.1117/12.630499.
[15]
Lee, Y.W. Power scaling of Yb3+-doped phosphate fiber lasers and amplifiers. Ph.D. Thesis, Stanford University, Stanford, CA, USA, 2008.