Study of the corrosion products formed on carbon steels in the tropical atmosphere of Panama

M ssbauer spectroscopy and X-ray powder diffraction (in selected samples) have been used to characterize corrosion products on carbon steels after atmospheric exposure to the tropical Panamanian locations of Panama and Colon, classified according to ISO 9223 as C3 and C5, respectively. Goethite (α-FeOOH) of intermediate particle size (20-100 nm), lepidocrocite (γ-FeOOH), a spinel phase consisting of non-stoichiometric magnetite (Fe3-xO4) and/or maghemite (γ-Fe2O3) and nano-sized particles were identified in the corrosion products. The spinel phase is related to short term atmospheric exposure transforms in time to other corrosion products. The corrosion resistance increased with fraction of goethite following a saturation-type behavior. Se caracterizaron los productos de corrosión de aceros al carbono expuestos a las atmósferas tropicales paname as localizadas en Panamá y Colón, mediante el uso de la espectroscopia M ssbauer y difracción de rayos-X (en muestras seleccionadas). Las atmósferas se clasifican como C3 y C5, respectivamente, de acuerdo a la norma ISO 9223. Se lograron identificar los compuestos goethita (α-FeOOH) de tama o de partícula intermedio (20-100 nm), lepidocrocita (γ-FeOOH), una fase de espinela consistente en magnetita no estequiométrica (Fe3-xO4) y/o maghemita (γ-Fe2O3), y nanopartículas. La fase de espinela se puede correlacionar con exposiciones cortas a la atmósfera, transformándose en el tiempo en otros productos de corrosión. La resistencia a la corrosión se incrementa con la cantidad de goethita siguiendo una conducta de saturación.