Caracterización microestructural y estabilidad térmica de la aleación Mg-23 %wt Zr sintetizada mediante Deposición Física en Fase Vapor (PVD)W

The objective of this work has been the study of the microstructure and the thermal stability of the alloy Mg-2.3 %Zr grown by Physical Vapour Deposition. This study has been carried out by Differential Scanning Calorimetry and Transmission Electron Microscopy. The alloy in the "as-deposited" condition consists of a solid solution of zirconium atoms in the magnesium matrix. The microstructure of the alloy is characterised by elongated grains oriented in the growth direction. These grains grow with the [0001] direction parallel to the deposit growth direction. During a continuous heating, the deposit shows three exothermal transformations which have been associated with a recovery process, the zirconium precipitation in the magnesium matrix and oxidation at high temperatures. The activation energy for the precipitation reaction calculated from Kissinger analysis is 139 kjmol-1. El objetivo del trabajo es estudiar la microestructura y estabilidad térmica de la aleación Mg-2,3 %wt Zr, crecida mediante deposición física en fase vapor. Las principales técnicas experimentales empleadas en este estudio son la calorimetría diferencial de barrido y la microscopía electrónica de transmisión. La aleación, en la condición estado de depósito (as-deposited)y es una solución sólida de átomos de circonio en magnesio. La microestructura de la aleación está caracterizada por granos alargados en la dirección de crecimiento. Los granos crecen con la dirección [0001] paralela a la dirección de crecimiento del depósito. Durante un calentamiento continuo del depósito, se observan tres transformaciones exotérmicas que se han asociado a restauración, precipitación del circonio en la matriz de magnesio y oxidación. Se calculó, mediante el análisis de Kissinger, que la energía de activación para el proceso de precipitación es de 138 kjmol-1.