Cinética de segregación de soluto a las dislocaciones parciales en Cu-5 % at. Mn

A model is proposed to describe, the kinetics of solute segregation to partial dislocations in solid solutions of cold-rolled alloys. The case for half-edge and half-screw dislocations is considered. The model gives account of the kinetic behaviour observed in a deformed Cu-5 at. % Mn alloy where two unknown processes were assessed during calorimetric isothermal experiments. The faster process corresponds to segregation to screw dissociated dislocations while the slower one corresponds to segregation to edge dissociated dislocations. Effective activation energies, larger for edge dislocations, are close to that for pipe diffusion along the partials corrected by pinner binding energy terms. It is also predicted that segregation occurs faster as the dislocation density is increased. Se propone un modelo para describir la cinética de segregación de soluto a las dislocaciones parciales en soluciones sólidas de aleaciones deformadas en frío. Se considera el caso en que la mitad de las dislocaciones son en arista y la otra mitad helicoidales. El modelo da cuenta del comportamiento cinético observado en aleaciones de Cu-5% at. Mn, durante las experiencias calorimétricas isotérmicas donde fueron estimados dos procesos. El proceso más rápido corresponde a segregación a las dislocaciones disociadas helicoidales, mientras que el más lento corresponde a la segregación a las dislocaciones disociadas en arista. Las energías efectivas de activación, las cuales son mayores para dislocaciones en arista, resultan ser cercanas a aquellas para la difusión tubular a lo largo de las componentes parciales, corregidas por términos de energía de interacción de anclaje. Se predice también que la segregación es más rápida cuando la densidad de dislocaciones aumenta.