Evaluación numérica del efecto del metal de soldadura sobre el factor de constricción en probetas C(T) bimetálicas

The effect of the weld metal on the out-of-plane constraint in C(T) bi-material specimens was studied using the Common Format Equation (CEE) and its associated constraint factor, Ω*, as a function of the thickness-to-ligament ratio, B/b. The values of Ω* for onematerial specimens (base metal) and bi-material specimens (base metal plus weld metal) were compared. The presence of weld metal lowers the degree of constraint in the bimaterial specimens in relation to the base metal specimens, for a given B/b value. This effect is attenuated for deeply cracked specimens, the Ω* values being similar for the onematerial and the bi-material specimens. El efecto del metal de soldadura sobre la constricción fuera-del-plano en probetas C(T) bimetálicas fue estudiado utilizando la Ecuación del Formato Común (EEC) y su factor de constricción asociado, Ω*, en función del cociente espesor de probeta a ligamento, B/b. Se compararon los valores de Ω* para probetas con sólo un material (metal base), y para probetas bimetálicas (metal base más metal de soldadura), constatándose que la presencia de metal de soldadura hace disminuir el grado de constricción en las probetas bimetálicas, con respecto a las probetas con sólo metal base. Este efecto se ve atenuado para grieta profunda, dando resultados similares para Ω* en las probetas con sólo metal base y bimetálica.