Oxidación cíclica de un acero refractario AISI 310 a alta temperatura en atmósferas con contenidos de oxígeno variables

High temperature oxidation tests of an AISI 310 stainless steel was performed in two different environments: in an standard atmosphere (21 % oxygen) at 704, 800, 884 and 1,000 °C and in the typical environment of a gas turbine and vapor generator of a combined-cycle electric generation unit (10 % oxygen) at 800 and 1,000 °C. The oxidation kinetics was determined by means of the measurement of the weight gain per unit surface of the specimen and also determining the thickness of the oxide layer. Comparable results have been obtained using both methodologies and the effect of the oxygen content along with the other experimental differences were determined observing the oxidation kinetics in both environments. The cyclic oxidation of AISI 310 deteriorates at temperatures higher than 1,000 °C. Se ha llevado a cabo un estudio experimental sobre la oxidación a altas temperaturas de un acero inoxidable refractario AISI 310, en dos ambientes diferentes: en una atmósfera convencional (21 % de O2), a 704, 800, 884 y 1.000 °C y en un ambiente simulativo de una turbina de gas y del generador de vapor de u a central eléctrica de ciclo combinado (10-11 % de O2), a 800 y 1.000 °C. La cinética de la oxidación del material se ha determinado a partir, tanto de la ganancia de peso por unidad de superficie experimentada por las probetas objeto de ensayo como por la determinación de los espesores de las capas de óxido formados. Se han obtenido resultados comparables con ambas metodologías y se ha puesto de manifiesto el efecto del contenido de oxígeno y de las demás diferencias experimentales a partir de la comparación de las cinéticas de oxidación del acero en los dos medios oxidantes analizados. La oxidación del acero AISI 310 en situaciones térmicas cíclicas empieza ya a ser importante a partir de una temperatura de 1.000 °C.