Mejora de la tenacidad de un acero de ultraalto contenido en carbono nnediante unión por laminación con un acero al cromo y molibdeno

Laminated composite materials containing five layers of ultrahigh carbon steel, 1.35%C, and five layers of a Cr-Mo steel were processed by roll bonding. The rolling procedure improves the bonding of layers and refines the microstructure, diminishing grain size and removing the pearlitic zones. Charpy impact tests were carried out to evaluate the impact properties. Toughness of the laminated composite was highly improved respect to the ultrahigh carbon steel. Moreover, it was double than that of the Cr-Mo steel in the arrester orientation. These results reveal the important role of the interfaces in the mechanical properties of the composite materials. Se procesaron mediante unión por laminación, dos materiales compuestos laminados de 10 capas: cinco capas de un acero de ultraalto contenido en carbono con 1,35 % C, alternadas con otras cinco de un acero al cromo y molibdeno. La laminación en caliente consolida la unión entre las capas y afina la microestructura, reduciendo el tama o de grano y eliminando las zonas de perlita presentes inicialmente. Se realizaron ensayos de impacto Charpy para evaluar su resistencia al impacto. El material compuesto laminado mejoró sustancialmente la tenacidad del acero de ultraalto carbono, además de duplicar la resiliencia del acero al cromo y molibdeno en la orientación "en serie". Estos resultados ponen de manifiesto la importancia de las intercaras en las propiedades mecánicas de los materiales compuestos.