Generación de inclusiones no metálicas y su efecto sobre el bloqueo de boquillas de colada continua en aceros ultra bajo carbono estabilizados con titanio

This work presents a thermodynamic and experimental analysis of the phases that precipitate in the non metallic inclusions depending on the contents of aluminium (Al), titanium (Ti) and oxygen (O) in the steel, and their influence on the nozzle clogging. For the thermodynamic analysis, the program FACT WIN (Facility For The Analysis of Chemical Thermodynamics) subroutine Equilib. was used. The experimental tests were carried out in an TAMMANN furnace, in an argon atmosphere. The control of the content of dissolved oxygen was carried out by means of sensors of solid electrolyte bases zirconia. The characterization of the inclusions was carried out with SEM, EDS and by means of the technique of fractional reduction with carbon. A good agreement was observed between the thermodynamic predictions and the experimental results. En este trabajo se presenta un análisis termodinámico y experimental de las fases que precipitan en inclusiones no metálicas en función de los contenidos de aluminio (Al), titanio (Ti) y oxígeno (O) en el acero y su influencia sobre el bloqueo de boquillas de colada continua. Para el análisis termodinámico se utilizó el programa FACT-WIN (Facility For The Analysis of Chemical Thermodynamics) subrutina Equilib. Las pruebas experimentales se realizaron en un horno TAMMANN, en atmósfera de argón. El control del contenido de oxígeno disuelto se llevó a cabo mediante sensores de electrólito sólido base zirconia. La caracterización de las inclusiones se realizó por SEM, EDS y mediante la técnica de reducción fraccionada con carbono. Se observó una buena concordancia entre las predicciones termodinámicas y los resultados experimentales.