Influencia del contenido de silicio y el tratamiento térmico en la resistencia al desgaste de fundiciones blancas al cromo en condiciones de rápida solidificación

The influence of silicon content and heat treatment on microstructure, abrasive and dry friction wear resistance of a 3 % C, 12 % Cr cast iron, under fast solidification conditions is studied. The fast solidification condition diminishes the carbide volume and the silicon content increases their dispersion and finesses. All matrixes obtained were perlitics, whit different finesses. No intermediate transformation products were noticed. Hardness had little variation. Austenization treatment show little affectivity, with tendency to increase wear in reference to as cast and maintenance treatments. Behavior under dry friction and abrasive wear were similar under test conditions applied whit more influence of carbide morphology in the abrasive wear conditions. Se estudia la influencia del silicio y el tratamiento térmico sobre la microestructura y la resistencia al desgaste abrasivo y por fricción seca de una fundición con 3 % C y 12 % Cr, obtenida en condiciones de rápida solidificación. La rápida solidificación disminuye el volumen de carburos, la finura y dispersión de éstos aumentan con el incremento del silicio. Todas las muestras presentaron matrices perlíticas, variando en finura con el tratamiento. No se apreciaron productos de transformación intermedios. Las durezas tuvieron poca variación. Los tratamientos de austenización mostraron poca efectividad, con tendencia a desgastes más elevados que en estado bruto de colada y con tratamiento de mantenimiento. Los comportamientos ante la abrasión y la fricción seca en las condiciones ensayadas fueron similares. Se evidenció alta influencia de la morfología de los carburos en el desgaste abrasivo.