Evaluaciones microcalorimétricas no-isotermas en aleaciones de Cu-9Ni-5,5Sn templadas y deformadas en frío

The thermal aging of both a quenched and a cold rolled homogeneous supersaturated Cu-9 % wt Ni-5.5 wt % Sn alloy has been studied from differential scanning calorimetry (DSC) and microhardness measurements. An increase of the hardness during the aging of the quenched sample, because of the precipitation of a Υ′ phase, takes place. On the contrary, no hardness increase was observed during the aging of the cold rolled sample. A theoretical analysis of the enthalpy determined from the first DSC exothermic peak suggests that a segregation of the solute towards the dislocations occurs during the aging of the cold rolled alloy. The values of the n Avrami-Erofeev coefficients estimated from the kinetic analysis supports the above interpretations. Se ha estudiado por calorimetría diferencial de barrido (DSC) y medidas de microdureza, el comportamiento durante el recocido de una aleación Cu-9 % Ni-5,5 % Sn templada y deformada por laminación en frio al 50 %, respectivamente. Se ha concluido que durante el tratamiento térmico de la muestra templada tiene lugar un aumento de la microdureza atribuido a la precipitación de una fase Υ′ de composición (CuxNi1x)3Sn. Sin embargo, no se ha observado un aumento de dureza durante el recocido de la muestra deformada en frío. Este comportamiento se ha interpretado considerando que las dislocaciones generadas por la laminación en frío, favorecen la segregación de soluto (níquel y esta o) hacia las dislocaciones en lugar de la formación de la fase (CuxNi1-x)3Sn. Tanto el análisis teórico de la entalpía determinada para esta etapa como los valores de los coeficientes n de Avrami-Erofeev determinados a partir de un análisis cinético apoyan esta interpretación.