Desarrollo y caracterización del material compuesto de base cobre reforzado con cerámicas intermetálicas de TiB₂

In this work, mechanical and electrical properties of copper base composites alloy sstrengthened by dispersed TiB2 particles are characterized. Powders of copper and TiB2 were mechanically ball milled in a planetary mill during 12 and 36 h under a protective atmosphere of argon. Resulting powders were compacted uniaxially at 923 K under 90 MPaduring 2 h. Part of these compacts were hot rolled at temperatures ranging between 1073 and 1023 K with 20 % reduction. Comparing the properties of materials after this thermomechanical process with that of as-consolidated, it was observed an electrical conductivity increase, and a decrease on hardness and ductility. En este trabajo se han caracterizado las propiedades mecánicas y eléctricas de materiales compuestos de base cobre reforzados mediante la dispersión de partículas de TiB2. Las mezclas cobre-cerámica, se obtuvieron por molienda mecánica de polvos de cobre y TiB2, en un molino planetario, durante 12 y 36 h bajo atmósfera de argón. El polvo resultante se compactó bajo una presión uniaxial 90 MPa durante 2 h a 923 K. Algunos de los compactos resultantes se laminaron a una temperatura comprendida entre 1073 y 1023 K hasta alcanzarse una reducción del 20 %. Comparando las propiedades de los materiales, tras este procesado termomecánico, con las propiedades de los materiales compactados uniaxialmente, se encontró que la laminación en caliente aumenta la conductividad eléctrica, pero da lugar a una disminución del valor de la dureza y la ductilidad.