Efecto de las condiciones de enfriamiento sobre la fracción y morfología de la fase primaria épsilon en una aleación comercial ACuZinc5TM

The mechanical properties of ACuZinc5TM alloys are influenced by the fraction solid of the primary epsilon (ε) phase and their interrelations with the eta (η) phase. In this study the primary epsilon phase fraction results from cooling conditions similar to that applied in different casting processes have been measured. Additionally an analysis was made from the morphology’s changes and from the thermal analysis results to suggest the probably adequate moment to apply stirring in semisolid metal processing. From these results it is possible to design experimental thermal cycles to obtain an adequate distribution of ε and η phases in the end castings microstructure. La fracción sólida de la fase primaria épsilon (ε) y su interrelación con la fase eta (η) influyen en las propiedades mecánicas de la aleación ACuZinc5TM. En este estudio se midió la fracción de fase épsilon primaria resultante de condiciones de enfriamiento similares a las que se utilizan en diferentes procesos de vaciado. Adicionalmente se realizó un análisis a partir de los cambios morfológicos de la fase primaria y de los resultados del análisis térmico para sugerir el momento probablemente adecuado para agitar el ba o metálico durante procesos de vaciado en estado semisólido. A partir de estos resultados es posible dise ar ciclos térmicos experimentales para obtener una apropiada distribución de las fases ε y η en la microestructura final de las piezas vaciadas.