EFFECTS OF HEAT TREATMENT AND ENVIRONMENT ON CRACK PROPAGATION RATE IN STEEL GC-4 UNDER CORROSION FATIGUE AND STRESS CORROSION

Comparative investigations were carried out of the effect of heat treatment regimes Jor steel GC-4(40CrMnSiMoVA)on its crack propagating rates,from corrosion fatigue, (da/dN)_(CF),or stress corrosion cracking,(da/dt)_(SCC),in media with various constituents and pH values.Both(da/dN)_(CF) and(da/dt)_(SCC) accelerate with the increase of yield stress of the steel,yet the former is far less than the later.In comparison with media,the (da/dt)_(SCC) in distilled water is slightly greater than that in 3.5% NaCl solution,and the (da/dN)_(CF) in distilled water is far less than that in 3.5% NaCl solution.With the pH value increasing in 3.5% NaCl solution,the(da/dN)_(CF) lowers down and the(da/dt)_(SCC) speeds up.An explanation was also proposed with concept of the cyclic hardening and softening at crack tip,as well as the crack closure and occluded cell effect.