SHORT FATIGUE CRACK BEHAVIOUR IN ISO-STRESS SPECIMENS

Fatigue tests were made on a vibration machine using specially designed specimens to investi- gate the initiation and propagation features of short fatigue cracks in a weld metal.The spec- imens were triangular in shape so that when loaded as a cantilever beam the surface tensile stress is constant.Test results show that short fatigue cracks mainly originate from slip bands within ferrite grains.The development of short fatigue cracks is marked by a gradual increase in crack density with fatigue cycles.Coalescence of short cracks leads to crack propagation and the crack path is predominantly transgranular.