MECHANISM DISCERNMENT OF CORROSION FATIGUE CRACK GROWTH FOR A537 STEEL AND INDUSTRIAL IRON IN 3.5% NaCl SOLUTION
|
Abstract:
The mechanism of corrosion fatigue crack growth for A537 steel and industrial iron in 3.5% NaCl solution was distinguished according to the effect of applied potential, micrograph of fracture surface and acoustic emission activity during crack growth. The