EFFECT OF CI- INDUCED ENBRITTLEMENT ON CORROSIVE WEAR OF 304 STEEL AND IT''S EVALUATION
Cl^—致脆对不锈钢磨蚀的影响及其判据研究

Static corrosion rate and corrosive wear loss of AISI304 stainless steel have been examined in 1 mol/L H2SO4 solution with different contents of Cl-. Specific energy consumption and the relationship betweem scratch length and energy consumption in above condition have been measured using single pendulum scratch device. Experimental results showed that the existence of Cl- enhanced the corrosion and corrosion wear for 304 steel and with increasing Cl-, specific energy consumption of material surface decreased. It was suggested that the enhancement of corrosive wear of 304 steel would be the environmental embrittlement resulting from Cl-.\=