Microstructural Evolution of Ti-5.6Al-4.8Sn-2Zr-1Mo-0.35Si-0.7Nd Titanium Alloy with Carbon Additions

The effect of carbon addition on microstructural evolution was studied in a near-α titanium alloy(Ti-5.6Al-4.8Sn-2Zr-1Mo-0.35Si-0.7Nd). It was found that flake and ribbon titanium carbides with a NaCl crystal structure formed in the as-cast alloys with carbon additions of over 0.17 wt pct. Flake carbide particles are the product of eutectic transformation and precipitate from the high-temperature β phase. The ribbon carbide particles are primary phases formed prior to the nucleation of any metallic phases. The as-cast alloys with carbide precipitation after heat-treatment atβt-30℃ followed by water quenching showed the spheroidization of α lamellae and partial dissolution of carbide particles. After annealing at βt 15℃, carbide particles are mostly distributed at the grain boundary and spheroidized through mixed grain boundary plus bulk diffusions.