Dielectric and Ferroelectric Properties of La-Doped SrBi2Nb2O9 Ceramics

Sr1-xLa2x/3Bi2Nb20O （0 ≤ x ≤0.2） ceramic samples are prepared by the solid-state reaction method. Their structure, dielectric and ferroelectric properties are investigated. The incorporation of La^3＋ improves the den- sification and decreases the grain size of the ceramics without changing the crystal structure. The remanent polarization 2PT increases with increasing La content and reaches a maximum value of 22.8μC/cm^2 at x = 0.125, which is approximately 60% larger than that of pure SrBi2Nb2O9. The Curie temperature keeps almost unchanged at a value of about 440℃. The relationship between doping and the ferroeleetrie and dielectric properties are discussed.