Observation of Ferroelectric Structures of Near-stoichiometric LiNbO3 Crystal and Its Mechanism
近化学计量比LiNbO3晶体电畴结构观察和机理探讨

Near stoichiometric LiNbO3 crystals of varied composition were grown by a double crucible Czochralski method. An etching method was applied to observe the ferroelectric domain structures of the as-grown crystals. The results show that the congruent crystal grown along z-axis contains a domain structure consisting of concentric rings. The crystal with composition of 49.4mol% Li2O contains a special domain structure consisting of three fan-shape opposite domains with three-fold symmetry, which is consistent with the symmetry of the crystal structure. The crystal with composition of 49.7mol% Li2O has a single domain structure. The formation mechanism of the domain structures was discussed based on a thermoelectric field model. It is argued that the sign of the temperature gradient along z-axis in the front of para- ferroelectric interface is the critical factor that determines the polarity direction of the domain in development. Finally, the technological methods to control the domain structures were discussed.