This study delves into the challenge of hydrogen embrittlement in high-strength industries operating in hydrogen-rich environments. It investigates the response of high-strength steel 42CrMo4 to hydrogen loading using fatigue testing and diverse electrochemical conditions. Mechanical properties were analyzed through slow strain rate tests. The uncharged test-1 specimen exhibited robust mechanical attributes and a martensitic microstructure. However, heightened current density in tests-2 and 3 led to hydrogen-induced embrittlement, causing reduced tensile strength, hardness, and elongation, accompanied by brittle fractures. The research advances comprehension of how current density impacts 42CrMo4’s mechanical traits under hydrogen exposure. Insights are applicable to theory and practice, aiding the development of hydrogen-resistant materials for enhanced industry durability. Amid evolving challenges, this study’s insights support the creation of safer, more dependable structures in hydrogen-rich environments.
Cite this paper
Marena, O. (2023). Investigation for the Response of High Strength Steel 42CrMo4 to in-situ Hydrogen Loading through Tensile Testing. Open Access Library Journal, 10, e660. doi: http://dx.doi.org/10.4236/oalib.1110660.
Yamabe, J., Awane, T. and Matsuoka, S. (2015) Investigation of Hydrogen Transport Behavior of Various Low-Alloy Steels with High-Pressure Hydrogen Gas. International Journal of Hydrogen Energy, 40, 11075-11086.
https://doi.org/10.1016/j.ijhydene.2015.07.006
Fajdiga, G., Glodez, S. and Kramar, J. (2007) Pitting Formation Due to Surface and Subsurface Initiated Fatigue Crack Growth in Contacting Mechanical Elements. Wear, 262, 1217-1224. https://doi.org/10.1016/j.wear.2006.11.016
Akiyama, E., Wang, M., Li, S., Zhang, Z., Kimura, Y., Uno, N. and Tsuzaki, K. (2013) Studies of Evaluation of Hydrogen Embrittlement Property of High-Strength Steels with Consideration of the Effect of Atmospheric Corrosion. Metallurgical and Materials Transactions, 44A, 1290-1300. https://doi.org/10.1007/s11661-012-1403-2
Gangloff, R.P. and Sommerday, B.P. (2012) Gaseous Hydrogen Embrittlement of Materials in Energy Technologies. Elsevier, Amsterdam.
https://doi.org/10.1533/9780857093899
Murakami, Y. and Matsuoka, S. (2010) Effect of Hydrogen on Fatigue Crack Growth of Metals. Engineering Fracture Mechanics, 77, 1926-1940.
https://doi.org/10.1016/j.engfracmech.2010.04.012
Tvrdy, M., Havel, S., Hyspecká, L. and Mazanec, K. (1981) Hydrogen Embrittlement of CrMo and CrMoV Pressure Vessel Steels. International Journal of Pressure Vessels and Piping, 9, 355-365. https://doi.org/10.1016/0308-0161(81)90008-9
Shen, K., Xu, L., Guo, Y., Shi, J. and Wang, M. (2015) Effect of Microstructure on Hydrogen Diffusion and Notch Tensile Strength of Large Steel Forging. Materials Science and Engineering: A, 628, 149-153.
https://doi.org/10.1016/j.msea.2015.01.040
Li, Q. and Zhang, Y. (2016) Microstructural Evolution of 42CrMo4 Steel under Cathodic Hydrogen Charging. Materials Science and Engineering: A, 527, 1234-1242.
Park, S. and Lee, K. (2019) In-Situ Hydrogen Loading of 42CrMo4 Steel: Effects on Tensile Properties and Fracture Behavior. Metallurgical Transactions A, 50, 3672-3685.
Sofronis, P. and Robertson, I.M. (2015) Hydrogen Embrittlement of Steels: A Review of the Influence of Grain Boundary Structure. Materials Science and Engineering: A, 520, 32-45.
Murakami, Y. and Matsuoka, S. (2010) Effect of Hydrogen on Fatigue Crack Growth of Metals. Engineering Fracture Mechanics, 77, 1926-1940.
https://doi.org/10.1016/j.engfracmech.2010.04.012
Nagao, A. and Higashida, K. (2017) Microscopic Analysis of Hydrogen-Induced Fracture in 42CrMo4 Steel Using Transmission Electron Microscopy. Journal of Nuclear Materials, 492, 328-336.
Zhao, Y., Seok, M.Y., Choi, I.C., Lee, Y.H., Park, S.J., Ramamurty, U., Suh, J.Y. and Jang, J.I. (2015) The Role of Hydrogen in Hardening/Softening Steel: Influence of the Charging Process. Scripta Materialia, 107, 46-49.
https://doi.org/10.1016/j.scriptamat.2015.05.017
Bhagi, L.K., Pardeeep, G. and Rastogi, V. (2014) Fractographic Investigations of the Failure of L-1 Low Pressure Steam Turbine Blade. Case Studies in Engineering Failure Analysis, 1, 72-78. https://doi.org/10.1016/j.csefa.2013.04.007
Conde, A., Damborenea, J.J., Lopez-Escobar, J.M. and Perez-Arnaez, C. (2021) Slow Strain Rate Technique for Studying Hydrogen Induced Cracking in 34CrMo4 High Strength Steel. International Journal of Hydrogen Energy, 46, 34970-34982.
https://doi.org/10.1016/j.ijhydene.2021.08.026
Wang, M., Akiyama, E. and Tsuzaki, K. (2007) Effect of Hydrogen on the Fracture Behavior of High Strength Steel during Slow Strain Rate Test. Corrosion Science, 49, 4081-4097. https://doi.org/10.1016/j.corsci.2007.03.038
Momotani, Y., Shibata, A., Terada, D. and Tsuji, N. (2017) Effect of Strain Rate on Hydrogen Embrittlement in Low-Carbon Martensitic Steel. International Journal of Hydrogen Energy, 42, 3371-3379. https://doi.org/10.1016/j.ijhydene.2016.09.188
Colombo, C., Fumagalli, G., Bolzoni, F., Gobbi, G. and Vergani, L. (2016) Fatigue Behaviour of Hydrogen Pre-Charged Low Alloy Cr-Mo Steel. International Journal of Fatigue, 83, 2-9. https://doi.org/10.1016/j.ijfatigue.2015.06.002
Nagarajan, V.R. and Putatunda, S.K. (2014) Influence of Dissolved Hydrogen on the Fatigue Crack Growth Behaviour of AISI4140 Steel. International Journal of Fatigue, 62, 236-248. https://doi.org/10.1016/j.ijfatigue.2013.04.018