Mechanical alloying of FeCoCr

Keywords: FeCo , FeCoCr , materials nanoestructurados , aleación mecánica , FeCo , FeCoCr , nanostructured materials , mechanical alloying

Full-Text   Cite this paper   Add to My Lib

Abstract:

The mechanical alloying of Fe-Co-Cr has been studied from the structural point of view by different techniques: XRD, TEM and M ssbauer spectroscopy, following the transformations taking place during milling. The alloys FeCo, Fe40Co50Cr10 and Fe50Co40Cr10 were prepared by milling of the elemental powders during 1, 2, 5, 10, 20, 40 and 60 h. The kinetics of alloy formation occurs by incorporation of Co and/or Cr in the Fe structure. For the Fe-Co alloy after 10h of milling a mixture of Fe (Co) solid solution and a-Fe is obtained. For the FeCoCr alloys prolonged milling results in Cr incorporation in the FeCo structure and a mixture of Fe (Co) and Fe (Cr) is formed. A grain size in the range of 2-5 nm is reached after 60h of milling El proceso de aleación mecánica de Fe-Co-Cr ha sido estudiado desde el punto de vista estructural por varias técnicas: DRX, MET, Espectroscopía M ssbauer, siguiendo las transformaciones que tienen lugar durante la molienda. Las aleaciones FeCo, Fe40Co50Cr10 y Fe50Co40Cr10 fueron preparadas a partir de los polvos elementales por molienda durante 1, 2, 5, 10, 20, 40 y 60 h. La cinética de formación de aleación ocurre por incorporación del Co y/o Cr en la estructura del Fe. Para la aleación Fe-Co después de 10 h de molienda se obtiene la mezcla de una solución sólida Fe (Co) y a-Fe. Para las aleaciones FeCoCr, la molienda prolongada resulta en la incorporación de Cr en la estructura de FeCo formándose una mezcla de Fe (Co) y Fe (Cr). Un tama o de grano en el orden de 2-5 nm es obtenido después de 60 h de molienda

Full-Text

comments powered by Disqus

Contact Us

service@oalib.com

QQ:3279437679

微信:OALib Journal