氯化丁基橡胶/丁腈橡胶宽温域阻尼材料的制备及性能研究

制备氯化丁基橡胶（CIIR）/丁腈橡胶（NBR）宽温域阻尼材料，研究CIIR/NBR并用比以及765树脂、木质纤维素和石墨烯的用量对并用胶阻尼性能的影响。结果表明：当CIIR/NBR并用比为30/70，765树脂、木质纤维素和石墨烯的用量分别为4，10和5份时，并用胶具有较宽的阻尼温域。;The CIIR/NBR damping material for wide temperature range application was prepared，and the effects of CIIR/NBR blending ratio，the amount of 765 resin，lignocellulose and graphene on the damping properties of the blends were investigated. The results showed that，when the CIIR/NBR blending ratio was 30/70，and the amounts of 765 resin，lignocellulose and graphene were 4，10 and 5 phr，respectively，the blends had a wide damping temperature range