Abstract:
本文采用黑龙江某工厂脱销过程中产生的废脱硝催化剂作为原料，每次取15 g废脱销催化剂，在高压釜中用氢氧化钠作浸出剂，研究氢氧化钠用量、浸出温度、浸出时间、液固比对浸出率的影响。实验结果表明：控制氢氧化钠用量为18 g，浸出温度140℃，浸出时间5 h，m(H2O)/m (催化剂) 6.7:1，搅拌速度为200 r/min时，钒和钨的浸出率都达到100%。
In this paper, the spent denitrification catalyst produced in the process of selling out of a factory in Heilongjiang province was used as raw material, and 15 g of spent denitrification catalyst was taken at each time. Sodium hydroxide was used as the leaching agent in the autoclave to study the effects of sodium hydroxide dosage, leaching temperature, leaching time and liquid-solid ratio on the leaching rate. The results showed that when the sodium hydroxide dosage was controlled at 17 g, the leaching temperature was 140？C, the leaching time was 5 h, the liquid-solid ratio was 6.7:1, and the stirring speed was 200/min, the leaching rates of vanadium and tungsten reached 100%.
| [1] | 杜譞, 朱留财. 氮氧化物污染防治的国外经验与国内应对措施[J]. 环境保护与循环经济, 2011, 31(4): 6-10. |
| [2] | 司蔚, 李晓弢, 谷雪景. 我国固定源大气污染物排放标准评析[J]. 环境保护, 2011(10): 50-51. |
| [3] | 杨刚. 《火电厂大气污染物排放标准》(GB13223-2011)对热电项目设备选型的影响[J]. 科技传播, 2013, 5(1): 24-25. |
| [4] | Seinfeld, J.H. (1986) Atmospheric Chemistry and Physics of Air Pollution. Environment Science & Policy for Sustainable Development, 68, 1595-1595. |
| [5] | 李远, 沈岳松, 祝社民, 等. 锆掺杂Ti-Ce-Ox复合氧化物NH3选择性催化还原NO的影响[J]. 硅酸盐学报, 2011, 39(6): 989-994. |
| [6] | Li, H., Zhang, S. and Zhong, Q. (2013) Effect of Nitrogen Doping on Oxygen Vacancies of Titanium Dioxide Supported Vanadium Pentoxide for Ammo-nia-SCR Reaction at Low Temperature. Journal of Colloid & Interface Science, 402, 190-195. https://doi.org/10.1016/j.jcis.2012.10.033 |
| [7] | Teng, H., Liyeh Hsu, A. and Lai, Y.C. (2001) Catalytic Reduction of NO with NH3 over Carbons Impregnated with Cu and Fe. Environmental Science & Technology, 35, 2369. https://doi.org/10.1021/es001674c |
| [8] | 高岩, 栾涛, 彭吉伟, 等. 燃煤电厂真实烟气条件下SCR催化剂脱硝性能[J]. 化工学报, 2013, 64(7): 2611-2618. |
| [9] | Forzatti, P. (2001) Present Status and Perspectives in de-NOx SCR Catalysis. Applied Catalysis A: General, 222, 221-236. https://doi.org/10.1016/S0926-860X(01)00832-8 |
| [10] | Lietti, L., Alemany, J.L., Forzatti, P., et al. (1996) Reactivity of V2O5-WO3/TiO2 Catalysts in the Selective Catalytic Reduction of Nitric Oxide by Ammonia. Catalysis Today, 29, 143-148. https://doi.org/10.1016/0920-5861(95)00250-2 |
| [11] | 云端, 邓斯理, 宋蔷, 等. V2O5-WO3/TiO2系SCR催化剂的钾中毒及再生[J]. 环境科学研究, 2009, 22(6): 730-735. |
| [12] | Shang, X., Hu, G., Chi, H., et al. (2012) Regeneration of full-Scale Commercial Honeycomb Monolith Catalyst (V2O5-WO3/TiO2) Used in Coal-Fired Power Plant. Journal of Industrial & Engineering Chemistry, 18, 513-519.
https://doi.org/10.1016/j.jiec.2011.11.070 |
| [13] | 李俊峰, 张兵兵, 李翼然. 基于钒钛基SCR法废脱硝催化剂的回收利用[J]. 广州化工, 2014, 42(24): 130-132. |
| [14] | 谢宗. 燃煤电厂废弃SCR催化剂中回收有价金属的研究[D]: [硕士学位论文]. 北京: 华北电力大学, 2016. |