聚甲基丙烯酸甲酯包覆十二醇微胶囊的制备及表征
|
Abstract:
以相变物质正十二醇（DA）为芯材，聚甲基丙烯酸甲酯（PMMA）为壁材，采用悬浮聚合法制备了正十二醇-聚甲基丙烯酸甲酯（DA@PMMA）微胶囊。通过差示扫描量热仪（DSC），扫描电镜（SEM），透射电镜（TEM），傅里叶变换红外光谱仪（FIIR）和热重分析仪（TGA）等仪器对微胶囊进行检测表征。结果表明：当工艺为苯乙烯-马来酸甘钠盐（SMA）加入量占DA质量的7.5%，偶氮二异丁腈（AIBN）加入量占单体甲基丙烯酸甲酯（MMA）质量的7.5%，芯材壁材质量比为2：1，搅拌速度为1 000 r/min时，所制备的微胶囊整体性能最好。DA@PMMA微胶囊为球形，平均粒径26 μm，DA@PMMA微胶囊中DA的质量分数为66%。DA@PMMA微胶囊的熔化焓和结晶焓分别是137.6 J/g和132.8 J/g。TGA和FIIR的分析表明，DA@PMMA微胶囊具有良好的性能。 The N-dodecanol-polymethyl-metharylate(DA@PMMA) microcapsules were prepared by suspension polymerization method with n-dodecanol (DA) as core material and polymethyl-metharylate (PMMA) as outer shell. Microcapsules were characterized by differential scanning calorimetry (DSC), scanning electron microscopy (SEM), transmission electron microscopy (TEM), fourier transform infrared spectroscopy (FTIR) and thermal gravimetric analysis (TGA), et al. The results show that the best conditions for preparation of DA@PMMA microcapsules are:Sodium salt of styrene-maleic anhydride polymer (SMA) content is 7.5% to DA, 2, 2-azobisisobutyronitrile (AIBN) content is 7.5% to methyl methacrylate (MMA), the core/shell mass ratio is 2:1, stirring speed is 1 000 r/min. DA@PMMA microcapsules are sphericalthe average particle size of DA@PMMA microcapsules is 26 μm. The mass fraction of DA in DA@PMMA microcapsules is nearly 66% and the latent heats of melting and freezing are found to be 137.6 J/g and 132.8 J/g. TGA and FIIR analyses also indicate that DA@PMMA microcapsules have good stability. 上海市“联盟计划”（LM201528）
| [1] | 余若冰, 彭少贤, 郦华兴. 微胶囊与微胶囊技术[J]. 现代塑料加工应用, 2000, 12(6):55-59. YU R B, PENG S X, LI H X. Microcapsule and microencapsulation technology[J]. Modern Plastics Processing and Applications, 2000, 12(6):55-59. |
| [2] | 张亮, 晏华, 余荣升, 等. 相变材料的研究进展及在建筑领域的应用综述[J]. 材料开发与应用, 2010, 25(1):69-73. ZHANG L, YAN H, YU R S, et al. A review of phase change materials:development and application in buiding energy saving[J]. Development and Application of Materials, 2010, 25(1):69-73 (in Chinese). |
| [3] | 于欣, 胡晓峰, 黄占华. 有机/复合相变储能材料研究进展[J]. 功能材料增刊Ⅰ, 2012(43):16-21. YU X, HU X F, HUANG Z H. Research progress in organic/composite phase change materials for energy storage[J]. Journal of Functional Materials SupplementⅠ, 2012(43):16-21. |
| [4] | 王建平, 张兴祥. 相变材料微胶囊研究进展[J]. 材料导报, 2007, 21(4):107-110. WANG J P, ZHANG X X. Recent progress in microencapsulated phase change materials[J]. Materials Review, 2007, 21(4):107-110. |
| [5] | CAO F Y, YANG B. Supercooling suppression of micro-encapsulated phase change materials by optimizing shell composition and structure[J]. Applied Energy, 2014, 111:1512-1518. |
| [6] | XU B, LI Z. Paraffin/diatomite composite phase change material incorporated cement-based composite for thermal energy storage[J]. Applied Energy, 2013, 105:229-237. |
| [7] | WANG Y, SHI H, XIA T D, et al. Fabrication and performances of microencapsulated paraffin composites with polymethylmethacrylate shell based on ultraviolet irradiation-initiated[J]. Materials Chemistry and Physics, 2012, 135:181-187. |
| [8] | YANG R, ZHANG Y, WANG X, et al. Preparation of n-tetradecane containing microcapsules with different shell materials by phase separation method[J]. Solar Energy Materials and Solar Cells, 2009, 93:1817-1822. |
| [9] | 李袆彧, 范亚明. 石蜡微胶囊的制备[J]. 广州化学, 2011, 36(4):36-40. LI Y Y, FAN Y M. Preparation of the microencapsulated paraffin[J]. Guangzhou Chemistry, 2011, 36(4):36-40. |
| [10] | SENNUR A, CEMIL A, FETHIYE G. Synthesis and characterization of poly(methyl-methacrylate)/n-hexadecane microcapsules using different cross-linkers and their application to some fabrics[J]. Thermochimica Acta, 2011, 518:1-8. |
| [11] | RAO Z H, WANG S F, PENG F F. Self diffusion and heat capacity of n-alkanes based phase change materials:A molecular dynamics study original research article[J]. International Journal of Heat and Mass Transfer, 2013, 64:581-589. |
| [12] | 吕刚, 缪春燕, 姚有为, 等. 二氧化硅凝胶包覆十二醇微囊的制备[J]. 化工新型材料, 2006, 34(11):26-28. LV G, MIAO C Y, YAO Y W, et al. Preparation of silica gel microcapsules containing lauryl alcohol[J]. New Chemical Materials, 2006, 34(11):26-28. |
| [13] | 余飞, 陈中华, 曾幸荣. 正十二醇相变储热微胶囊的制备与表征[J]. 高分子材料科学与工程, 2009, 25(6):135-138. YU F, CHEN Z H, ZENG X R. Preparation and characterization of thermal energy storage microcapsulated n-dodecanol by phase change[J]. Polymer Materials Science and Engineering, 2009, 25(6):135-138. |
| [14] | 王立新, 任晓亮, 任丽, 等. 原位聚合法制备相变材料微胶囊及其致密性[J]. 复合材料学报, 2006, 23(2):53-58. WANG L X, REN X L, REN L, et al. Preparation and penetrability of microcapsulated phase change materials[J]. Acta Materiae Compositae Sinica, 2006, 23(2):53-58. |
| [15] | MA S, SONG G L, LI W, et al. Uv irradiation-initiated mma polymerization to prepare microcapsules containing phase change paraffin[J]. Solar Energy Materials & Solar Cells, 2010, 94:1643-1647. |
| [16] | 宋晓秋, 刘钦矿, 段玉萍, 等. 安全脲醛树脂相变微胶囊制备及性能[J]. 高分子材料科学与工程, 2015, 7:129-134. SONG X Q, LIU Q K, DUAN Y P, et al. Preparation and performance analysis of security urea-formaldehyde resin phase change microcapsules[J]. New Chemical Materials, 2015, 7:129-134. |
| [17] | CHEN Z H, YU F, ZENG X R, et al. Preparation, characterization and thermal properties of nanocapsules containing phase change material n-dodecanol by miniemulsion polymerization with polymerizable emulsifier[J]. Applied Energy, 2012, 91:7-12. |
| [18] | MA Y J, ZONG J W, LI W, et al. Synthesis and characterization of thermal energy storage microencapsulated n-dodecanol with acrylic polymer shell[J]. Energy, 2015, 87:86-94. |